电站锅炉关键部件材料高温蒸汽氧化研究进展.pdfVIP

第34 卷 第1 期 中国腐蚀与防护学报 Vol.34 No. 1 2014 年2 月 Journal of Chinese Society for Corrosion and Protection Feb. 2014 电站锅炉关键部件材料高温蒸汽氧化 研究进展 鲁金涛 谷月峰 西安热工研究院有限公司 西安 710032 摘要：因其特殊的服役环境，电站锅炉关键材料需要同时满足力学性能与抗高温腐蚀性能的需求。本文从高 温蒸汽氧化的角度，讨论了现有锅炉合金及下一代电站合金的高温蒸汽腐蚀研究进展和高温蒸汽氧化机理。 关键词：蒸汽氧化 低合金钢 Cr 钢 奥氏体钢 高温合金 中图分类号：TG 172.82 文献标识码：A 文章编号：1005-4537(2014)01-0019-08 High-temperature Steam Oxidation Behavior of Alloys Used for Key Parts of the Power Plant Boiler LU Jintao, GU Yuefeng Xian Thermal Power Research Institute Co., Ltd., Xian 710032, China Abstract: Alloys used for power station boilers need to meet simultaneously the requirements of the high temperature mechanical properties and corrosion resistance because of the harsh service environment. The purpose of this paper is to review the existing information regarding steam oxida- tion behavior and oxidation mechanism of alloys, which are used for the present power plant boiler and designed to be used in next generation power station. Key words: steam oxidation, low-alloy steel, Cr steel, austenitic steel, superalloy 1 前言 律延续了按Cr 含量(质量分数) 划分的标准，主要分 电站锅炉关键部件材料主要指电站锅炉受热面 为低合金钢(1%~3%Cr)、铁素体/马氏体钢(9%~ 部件水冷壁、过热器、再热器用高压锅炉管，以及集 12%Cr) 和奥氏体钢(18%~25%Cr) 3 类。Cr 不仅是 箱、主蒸汽管道所用材料。这些部件所需要的压力 金属材料合金化设计的重要元素，同时也是合金表 等级、高温强度、持久强度、冲击性能等要求不尽相 面能否形成稳定、致密的保护性氧化膜的关键。如， 同，但是对于抗高温蒸汽氧化性能的要求是一致 低合金钢由于较低的Cr 含量不具有抗高温蒸汽氧 的。近年来，氧化层的隔热作用引起金属超温、氧化 化能力；9%Cr 钢的蒸汽氧化速率限制其使用温度不 皮的剥落在弯头等处堵塞引起超温爆管、剥落的氧 高于600 ℃，12%Cr 铁素体/马氏体钢抗蒸汽氧化能 化物颗粒对汽轮机前级叶片和喷嘴等的冲蚀等事故 力稍高一些；Cr 含量越高，奥氏体不锈钢越不容易 严重影响了机组运行的安全性、可靠性和经济性。 受腐蚀，25