(6307)--弯曲荷载作用下粉煤灰混凝土抗盐冻性能研究.pdfVIP

弯曲荷载作用下粉煤灰混凝土抗盐冻性能研究 摘 要: 为研究弯曲荷载作用下粉煤灰混凝土的抗盐冻性能，本文设计制作了不同粉煤灰掺量的钢筋混凝土试块在 3.5%NaCl 溶液中进行的快速冻融循环试验，对其施加不同水平的弯曲荷载，通过测量损伤后试块的动弹性模量，分 析粉煤灰掺量以及弯曲荷载对混凝土试块盐冻损伤的影响。研究结果表明：粉煤灰掺量为20%时可有效改善混凝土 的抗盐冻性能；弯曲荷载加剧了粉煤灰混凝土的盐冻损伤。 关键词: 弯曲荷载 粉煤灰混凝土 冻融循环 盐冻损伤; ; ; 中图法分类号: TU528.45 文献标识码:A 文章编号:1000-2324(2020)03-0556-03 Study on Salt Freezing Resistance of Fly Ash Concrete under BendingLoad LIUXing-juan,KANGXi-ning,LIUYan* Collegeof UrbanandRural Construction/HebeiAgricultural University,Baoding 071001, China Abstract: To study the salt-freezing resistance of fly ash concrete under bending load, a rapid freeze-thaw cycle test of reinforced concretetestblockswithdifferentamountsofflyashin3.5%NaClsolutionwasdesignedandfabricated.Inthispaper,bymeasuringthe dynamicelasticmodulusafterthedamage,theeffectsofflyashcontentandbendingloadonthesaltfreezedamageoftheconcretetest block were analyzed. The research results show that:when the content of fly ash is 20%, it can effectively improve the salt frost resistanceofconcrete;bendingloadexacerbatesthesaltfreezedamageofflyashconcrete. Keywords:Bendingload;fly ash concrete;freeze-thaw cycle;salt frost damage 混凝土结构是目前土木工程中最常见的结构形式，常应用于房屋建筑、跨海桥梁、公路、海底 [1] 隧道和海岸港口等 。其中，处于严寒地区海洋环境中的混凝土结构主要受到冻融循环、氯盐侵蚀 [2] 和弯曲荷载等破坏因素协同作用 ，为降低破坏过程中混凝土的损伤程度，保证混凝土材料在使用 [3-5] [6-8] 过程中的安全性和耐久性 、开展在多种破坏因素协同作用下的混凝土劣化机理研究 成为诸多专 家学者越来越关心的问题。本试验以不同粉煤灰掺量的钢筋混凝土构件为研究对象，进行弯曲荷载 作用下粉煤灰混凝土抗盐冻性能分析。 1 试验设计 本试验采用P.O42.5普通硅酸盐水泥，Ⅱ级粉煤灰，细骨料采用细度模数为2.74 且级配良好的 河砂，粗骨料选用粒径为5~20mm 连续级配的碎石，聚羧酸系高性能减水剂，引气剂是能溶于水的 K12 型白色粉末。混凝土配合比如表 1。 表 1 混凝土配合比 Table 1Concretemix ratio 分组 粉煤灰掺量/% 水泥/kg 粉煤灰/kg 水/kg 砂/kg 石/kg 减水剂/% 引气剂/% Group Fly ash admixture Cement Fly ash Water Sand Stone