304不锈钢板的钝化处理及耐蚀性

PassivationTreatmentandCorrosionResistanceof304StainlessSteelPlate

仝源

(南京科技职业学院，江苏南京210048)

TONGYuan

(NanjingPolytechnicInstitute,Nanjing210048,China)

摘要：使用硝酸和重珞酸钾的混合液对304不锈钢板进行了钝化处理。研究发现：不锈钢表面钝

化过程伴随着钝化膜的生成和溶解。与304不锈钢板相比，钝化膜中铬和氧的质量分数提高。钝

化膜主要由金属氧化物和金属氢氧化物构成。经过钝化处理后，304不锈钢板的自腐蚀电位正移，

自腐蚀电流密度降低，膜电阻升高，耐蚀性增强。

关键词：304不锈钢板；钝化膜；耐蚀性

Abstract:304stainlesssteelplatewaspassivatedinamixtureofnitricacidandpotassiu

dichromate.Itwasfoundthatthepassivationofstainlesssteelwasaccompaniedbytheformation

anddissolutionofpassivationfilm.Comparedwith304stainlesssteelplate,themassfractionof

chromiuandoxygeninthepassivationfilwereincreasedobviously.Thepassivationfilwas

composedofmetaloxideandmetalhydroxide.Afterpassivationtreatment,theself-corrosion

potentialof304stainlesssteelmovedtowardsthepositivedirection,theself-corrosioncurrent

densitywasdecreasedandthefilresistancewasincreased,thusresultingintheimprovementof

corrosionresistance.

Keywords：304stainlesssteelplate；passivationfil；corrosionresistance

中图分类号：TG174文献标志码：A文章编号2020

304不锈钢板。工艺流程为：砂纸打磨一超声波

0前言

处理一烘干一钝化一＞质量分数为5%的重铬

不锈钢是一种具有综合性能的合金钢，已广泛酸钾封闭10min—质量分数为1%的氢氧化钠中

应用于汽车、化工、航空航天等领域X。自然条件和一水洗一烘干。

下，不锈钢表面形成的氧化膜疏松、不均匀，防护性1.3性能测试

能较差。由于不锈钢具有良好的钝化特性，所以常使用S3400N型扫描电子显微镜观察304不锈

采用钝化处理提高不锈钢的耐蚀性卩7。本文使用钢板和钝化膜的表面形貌。使用EDX3200S型X

硝酸和重铬钾的混合液对304不锈钢