MMMMMMMMMMMMMMMMMMMMMMMMMMMMMMMMMMMMMMMMMMMEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEECHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHCHAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAANNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIICCCCCCCCCCCCCCCCCCCCCCCCCCCCCCCCCCCCCCCCCCCAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAAALLLLLLLLLLLLLLLLLLLLLLLLLLLLLLLLLLLLLLLLLLLEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEENNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGGIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIIINNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNNEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEEERRRRRRRRRRRRRRRRRRRRRRRRRRRRRRRRRRRRRRRRRRR

MECHANICALENGINEER

MECHANICALENGINEER

一种复合结构箍带断裂失效分析

孙越，张栓，刘洋，迟岑

（中国航发沈阳黎明航空发动机有限责任公司，沈阳110043）

摘要：针对一种复合结构箍带在工作过程中多发的断裂问题，通过对可能造成问题的各主要因素进行系统排查、分析和验

证，最终确定了箍带断裂的机理：工作过程中，箍带组件处于较大的振动环境中，箍带及支架在综合应力的作用下，在箍带组件靠近外

边缘两焊点处形成应力集中，而箍带的疲劳性能低于支架，从而在应力集中的位置发生疲劳破坏导致箍带断裂。通过采用将焊接结构改为机

械连接结构的措施优化设计，消除了应力集中作用，有效避免此类问题的再次发生。

关键词：箍带；应力集中；疲劳破坏；仿真分析；振动

中图分类号:V263.6文献标志码:粤文章编号：员园园圆原圆猿猿猿（圆园21）02原园026原园4

FractureFailureAnalysisofaCompositeStructureBand

SUNYue,ZHANGShuan,LIUYang,CHICen

(AECCShenyangLimingAero-engineCo.,Ltd.,Shenyang110043,China)

Abstract:Aimingatthefracturefailureofacompositestructurebandduringwork,themainfactorsthatmaycauseband

breakagearesystematicallyinvestigated,analyzedandverified.Themechanismoftheprob