焦作煤在首钢高炉的应用.pdfVIP

焦作煤在首钢高炉的应用 王冬青 竺维春 （首钢技术研究院，北京 100043 ） 1 摘 要 本次主要进行了焦作煤的实验室研究工作，完成了其工业分析、元素分析、燃烧性、可磨性、爆炸性等研 究，并与首钢现用煤种进行了对比分析。焦作煤与首钢现用的A 煤性能接近，其硫含量较A 煤低，主要缺点是可 磨性差，根据此特点制粉作业区采取了一系列措施确保了焦作煤在炼铁厂1 号高炉的工业试验验取得了成功，焦作 煤最高配喷比例为50%，试验期间高炉顺行状态良好。 关键词 焦作煤 基础性能 工业试验 Pulverized Jiaozuo Coal Injection Test in Shougang Blast Furnace Wang Dongqing Zhu Weichun (Shougang Research Institute of Technology, Beijing, 100043) Abstract Some laboratory’s studies are carried out about Jiaozuo coal pulverized into blast furnace, such as technical analysis, element analysis, combustibility, grindability and explosiveness etc. Its performance is similar to Yangquan coal. Its main disadvantage is lower grindability, According to this disadvantage, powder manufacturing took a series of measures to assure the industry test. The test of pulverized Jiaozuo coal into No.1 blast furnace was success. The highest proportion of Jiaozuo coal was 50%, and the blast furnace was in a good condition. Key words Jiaozuo coal, basic performance, industry test 高炉实施喷吹煤粉生产，是降低炼铁生产成本，提高企业经济效益最有效的途径。随着国内钢铁产能的 日益增大及高炉煤粉喷吹关键技术的不断进步和完善，市场需求逐渐扩大，特别是近年来随着优质炼焦煤资 源的日渐匮乏，高炉喷吹煤在钢铁冶炼工艺环节的地位日益提高。同时增收节支降成本的压力也不断加大， 故首钢炼铁厂不断开发新喷吹煤资源，以保首钢高炉喷煤指标的实现[1] 。 1 焦作煤实验室研究 本次研究的焦作煤来源于焦作煤业集团，其前身是焦作矿务局，是全国主要无烟煤生产基地之一，下属 22 个子公司、17 个分公司，其中煤炭生产矿井 11 个，核定生产能力 630 万吨/年。矿区保有储量为26.38 亿吨。焦作矿区东西长60km，南北宽20km，含煤面积971km2 ，预测煤炭储量80 亿吨。现浅部及开采条件 简单的区域基本开采结束，所剩区域大多埋藏较深和开采技术条件极为复杂的地区。主要产品是烧结用煤和 喷吹煤，发往本钢、武钢、马钢等钢铁企业。 王冬青，女，硕士，工程师，主要从事高炉喷吹煤研究，wangdongqing@ 焦作煤在首钢高炉的应用 8-419 1.1 工业分析 高炉喷吹用煤的煤种、煤质对高炉冶炼过程及技术经济指标有重要影响，煤的工业分析结果是选择喷吹 工艺方案时不可缺少的重要依据。煤的工业分析采用G B/T 212 的方法。将焦作煤与首钢现用A 煤、B 煤进 行了比较，由表1 可见，焦作煤和A 煤