钢包周转周期与温降研究.pdfVIP

钢包周转周期与温降研究 1 1 1 1 2 刘金刚 李战军 王文军 姜中行 朱志远 （1.首钢技术研究院，北京100043； 2.秦皇岛首秦金属材料有限公司，秦皇岛066326 ） 摘 要 通过对某中厚板厂100t钢包的周转和温降进行研究，得出了钢包空包的温降规律，当放置时间超过75min 后钢包温度基本低于800℃，在现有周期100min左右条件下，钢包无法满足温度要求。通过减少周转钢包数、缩短 浇次连浇炉数、加强钢包烘烤等措施使钢包周转周期由 102min降为73min，降低钢包温降 11.5℃，使LF炉电耗下 降5kW ·h/t 以上。1 关键词 钢包 周转 温降 周期 Research on Ladle Operating Cycle and Temperature Drop Liu Jingang1 Li Zhanjun1 Wang Wenjun1 Jiang Zhonghang1 Zhu Zhiyuan2 （1. Technical Research Institute, Shougang Group, Beijing, 100043; 2. Shouqin Company Ltd., Qinhuangdao, 066326) Abstract Research on ladle operating cycle and temperature drop in one of heavy and medium plate, concluded the temperature drop in empty ladle cant satisfy temperature requirements, when the ladle temperature is below 800 ℃, placed time longer than 75min in the present cycle around 100min. Ladle cycle time drop from 102 min to 73 min, reduce the temperature drop to 11.5 ℃, the power consumption of LF falls more than 5kW ·h/tons, by reducing the number of ladle, shorten the cycle number casting, strengthen the ladle baking measures. Key words ladle, operating cycle, temperature drop, cycle time 1 引言 在目前钢铁市场日益向高技术含量高附加值发展的前提下，对于中厚板市场的大量钢种开发中钢的成份 除要求钢材具有各项优异的力学性能外大部分均要求低碳或超低碳成份控制，如管线钢X70 、管线钢X80 、 低温压力容器、高强结构钢、高强建筑用钢、海洋平台用钢、E级和F级船板等[1, 2]，而目前冶炼此类钢种一 般工艺路线为转炉—LF精炼—真空处理—CC，这样真空处理无法发挥脱碳的功能，因此必须防止LF精炼增 碳，而对LF增碳影响最大的就是加热时间，而防止加热时间过长就必须控制钢水的温降和钢包的温降，掌 握钢包运行规律，实施生产流程中钢包周转的系统调控势在必行[3]，同时有效节约能源也是钢铁工业重要研 究课题之一[4,5] 。某钢厂现有铁水预处理装置2 套，100 吨转炉3 座，吹氩站3 座，LF精炼炉3 座，双工位 RH真空处理精炼设备一套，厚板坯连铸机2 台；由于该厂钢包无法进行在线烘烤，所以钢水出钢过程温降 过大一直是困扰该厂稳定生产的环节之一，为了找出钢水温降的限制性环节，减小钢水温降，对该厂的钢包 周转和钢水温降原因进行了研究。 11刘金刚，男，博士，高级工程师，从事纯净钢工艺技术开发，liujg9916@163.com 钢包周转周期