板坯连铸黏结漏钢控制技术的工艺改进.pdfVIP

1 板坯连铸黏结漏钢控制技术的工艺改进 邱刚祥 杨建华 巨银军 丁金虎 唐卫红 （湖南华菱湘潭钢铁有限公司，湘潭 411101 ） 摘 要 本文通过对湘钢板坯连铸生产中黏结漏钢事故的主要原因及特点进行分析，从工艺、操作和设备三个方面 的影响出发，结合生产实践，进而提出了有特色的“四看四确定安全浇钢法”的科学操作模式，有效地预防了铸机 黏结漏钢的产生，并取得了很好的实际的效果。 关键词 板坯连铸 黏结漏钢 四看四确定安全浇钢法 The Improvement of Control Technology About Sticking Breakout in Slab Continuous Casting Qiu Gangxiang Yang Jianhua Ju Yinjun Ding Jinhu Tang Weihong （Hunan Hualing Xiangtan Iron Steel Co., Ltd. ，Xiangtan ，411101 ） Abstract This article introduces the main causes and characteristic of the sticking breakout accident in slab continuous casting in heavy plate mill of XISC. From the effects of process, operation and equipment, it had been advanced of the scientific and characteristic operation mode of “4-look 4-confirm safe casting operation” in accordance with production practice. It has been effectively preventing the breakout in slab casting. It has obtained the practical improved result. Key words continuous casting, sticking breakout, 4-look 4-confirm safe casting operation 1 引言 板坯浇铸漏钢是板坯连铸生产中的恶性事故。近年来，随着工艺设备与技术的进步，比如结晶器漏钢预 报技术的应用、结晶器保护渣的技术进步等，使连铸机漏钢事故得到了大幅度减少，但由于涉及的因素、状 态和参数较多，对漏钢的控制技术仍属于板坯连铸的技术难题之一。 2 简介 华菱湘潭钢铁公司宽厚板厂（简称湘钢宽厚板厂）是我国新建的中厚板生产基地，现有两台 SVAI 连铸 机。1 号机为板坯连铸机，于 2005 年 4 月 3 日投产，2 号机为方板坯连铸机，于 2007 年 5 月 19 日投产，由 于两台铸机均没有上结晶器漏钢预报的监控系统，投产初期共发生过 7 次漏钢事故，其中有 6 次是黏结漏钢， 对生产、设备及成本均造成了巨大的损失。 总结这 7 次漏钢事故的原因，黏结漏钢是主要的事故原因，而影响黏结漏钢的因素有很多，其中主要的 有保护渣及保护渣相关操作，也与钢液条件、设备的精度和振动等有关。 邱刚祥，从事方板坯连铸工艺技术研究与管理。 8-538 第八届（2011 ）中国钢铁年会论文集 3 黏结漏钢产生的机理 所谓的黏连漏钢是指结晶器内，弯月面部位铜板与坯壳之间没有液渣渗入，导致气隙无法被填充，严重 时坯壳与铜板发生黏结，当铸坯下拉时摩擦阻力增大，黏连处被拉断，并向下和两边发展形成V 形破裂线， 到达结晶器口时就发生漏钢（见图 1）。 图1 黏结漏钢产生过程示意 图2 恶化润滑状况示意 1—被黏