Effect of Drying Time on the Antimony Doped Tin Dioxide
Coated Titanium Electrode#
5
10
15
20
25
30
35
40
Abstract: The antimony doped tin dioxide coated titanium electrodes were prepared by dip-coating
pyrolysis method with different drying time. The effect of drying time on the electrode activity,
morphology, crystallinity and composition were discussed. The results indicated that electrode
prepared by drying 10 minutes had higher activity towards phenol degradation than those prepared by
drying 0 or 30 minutes. The relation between the activity and oxygen vacancies concentration was
discussed. The TG-DTA analysis was used to monitor the reactions occurred during the electrode
preparation. The results showed that there were three endothermic or exothermal peaks and the possible
reactions were discussed.
Key words: Environmental engineering; antimony doped tin dioxide; drying; electrochemical; coating
0 Introduction
Antimony doped tin dioxide coated titanium electrode has attracted considerable
research interest in recent years in electrochemical degradation of toxic organic
contaminants in wastewater [1-5] and electrolytic generation of ozone due to its high
efficiency and non lead-containing [6,7]. It has higher oxygen evolution potential which
can hinder the thermodynamically favored oxygen evolution reaction, hence improve
the efficiency for organic destruction [8-10]. The electrodes have been usually prepared
by dip-coating pyrolysis method, sputtering method and chemical vapor deposition
method etc [1,11-13]. The dip-coating pyrolysis method has been often used to prepare
antimony doped tin dioxide electrodes due to its easy operation [14, 15]. This method
always includes coating the metal chloride alcoholic solution onto titanium substrate,
then drying at a temperature ranging from room temperature to 150 ℃ in an oven, and
finally baking in a furnace at a higher temperature of 400-600 ℃. This coating, drying
and baking process is repeated for 7-30 ti