转炉冶炼钢中氮含量的控制.pdfVIP

2010 年第 1 期 本钢技术 11 转炉冶炼钢中氮含量的控制 祝真祥 （本钢炼钢厂，辽宁本溪 117021 ） 摘 要：随着汽车板、管线钢的批量生产，对钢中氮含量的要求越来越高，通过炼钢转炉生产实践， 分析终点氧、补吹、全程复吹、钢包包况、底吹氩控制、脱氧合金化、降温料加入量对钢中氮的影响， 找到转炉生产过程中控制钢中氮的工艺措施，降低了钢中氮的含量，极大地提高了钢水的质量。 关键词：炼钢；钢中氮含量；钢水质量；终点氧；脱氧合金化 中图分类号：TF71 文献标识码：B Study on Controling of Nitrogen in Converter Steel ZHU Zhenxiang (Steel Making Plant，BX STEEL ，Benxi Liaoning 117021) Abstract ：With the mass production of car panels and linepipe steel, the nitrogen content in the steel is increasingly demanded. Briefed in the paper through the production of converter steel-making practice, analysis of the oxygen activity of the steel, second-blowing, blowing the whole complex, ladles situation 、 Argon-blowing controling, deoxidation and alloying, the temperature reduction material addition and so on are expected to influence nitrogen content in steel, to find a process to control nitrogen in the converter steel, reducing the nitrogen content in steel has greatly improved the quality of molten steel. Keywords: steelmaking；nitrogen content in steel ；steel quality；oxygen activity ；dioxidation and alloying 随着钢铁行业的高速发展，对钢材深冲性、高 含量在开吹过程中急剧下降，当硅锰基本氧化完全 强度、高温塑性的要求越来越高。氮作为钢中的元 时钢水中氮含量达到 0.002 5%～0.004 0%，在脱碳 期间则缓慢下降，在碳含量为 0.20 ％左右时降至最 素之一，大多数情况下是作为杂质元素存在的，严 低，约为 0.001 0%～0.001 5%，随着碳的降低、钢 重影响钢的高温强度和高温塑性，降低钢的深冲性