60Si2Mn的热处理性能研究毕业论文.docVIP

摘 要 通过对60Si2Mn进行均匀化退火、奥氏体化、正火和回火处理，研究这种材料在高温退火和回火处理下得到的组织，以及对这种材料的力学性能进行测试。通过光学显微镜(OM),硬度计对60Si2Mn组织和性能进行分析。结果表明，珠光体的片层间距随转变温度的降低而减小，不受奥氏体化温度和奥氏体晶粒大小的影响。珠光体是一种硬而脆的组织。60Si2Mn在均匀化退火后可以得到均匀的组织。在相同的时间下等温，温度越高60Si2Mn析出的碳化物等组织越多。 关键词：退火，正火，组织，性能 ABSTRACT By 60Si2Mn the homogenization, austenitizing, normalizing and tempering treatment, study the material at high temperature annealing and tempering with the next to get the organization, as well as the mechanical properties of this material for testing. By optical microscopy (OM), hardness and properties of 60Si2Mn analysis. The results show that the pearlite lamellar spacing with the transition temperature decreases, from austenitizing temperature and austenite grain size. Pearlite is a hard and brittle tissue. 60Si2Mn after the homogenization of the tissue can be uniform. At the same time the lower temperature, the higher the temperature carbide precipitation and other organizations 60Si2Mn more. Keywords: Annealing, Normalizing, Organization, Performance 毕业设计（论文）原创性声明和使用授权说明 原创性声明 本人郑重承诺：所呈交的毕业设计（论文），是我个人在指导教师的指导下进行的研究工作及取得的成果。尽我所知，除文中特别加以标注和致谢的地方外，不包含其他人或组织已经发表或公布过的研究成果，也不包含我为获得 及其它教育机构的学位或学历而使用过的材料。对本研究提供过帮助和做出过贡献的个人或集体，均已在文中作了明确的说明并表示了谢意。 作 者 签 名：　　 　 　　日　 期：　　 　 　　 指导教师签名：　　 　 　　 日　　期：　　 　 　　 使用授权说明 本人完全了解 大学关于收集、保存、使用毕业设计（论文）的规定，即：按照学校要求提交毕业设计（论文）的印刷本和电子版本；学校有权保存毕业设计（论文）的印刷本和电子版，并提供目录检索与阅览服务；学校可以采用影印、缩印、数字化或其它复制手段保存论文；在不以赢利为目的前提下，学校可以公布论文的部分或全部内容。 作者签名：　　 　 　　 日　 期：　　 　 　　 学位论文原创性声明 本人郑重声明：所呈交的论文是本人在导师的指导下独立进行研究所取得的研究成果。除了文中特别加以标注引用的内容外，本论文不包含任何其他个人或集体已经发表或撰写的成果作品。对本文的研究做出重要贡献的个人和集体，均已在文中以明确方式标明。本人完全意识到本声明的法律后果由本人承担。 作者签名： 日期： 年 月 日 学位论文版权使用授权书 本学位论文作者完全了解学校有关保留、使用学位论文的规定，同意学校保留并向国家有关部门或机构送交论文的复印件和电子版，允许论文被查阅和借阅。本人授权　　 　 　大学可以将本学位论文的全部或部分内容编入有关数据库进行检索，可以采用影印、缩印或扫描等复制手段保存和汇编本学位论文。 涉密论文按学校规定处理。 作者签名： 日期： 年 月 日 导师签名： 日期： 年 月 日 目 录 摘 要 I ABSTRACT II 第一章 文献综述 1 1.1 引言 1 1.2 60Si2Mn概述 2 1.3 等温处理 6 1.4 力学性能 8 第二章 实验方案及过程 15 2.1 实验方案 15 2.2