热压含碳球团强度影响因素的研究.pdfVIP

热压含碳球团强度影响因素的研究 李军，吉强，李鹏* （中国矿业大学(北京)化学与环境工程学院，北京 100083） 摘要：重点研究了原料水分、粒度和加热时间对热压含碳球团强度的影响，并对影响机理进 行了分析。实验结果表明：原料水分对热压含碳球团的强度影响较小；原料粒度包括煤粒度 和矿粒度对热压含碳球团的强度影响高度显著，煤 0.18mm、矿 0.45mm 时热压含碳球团的 强度达到 270kg/个；加热时间对热压含碳球团的强度影响高度显著，在本次试验条件下加热 时间取 30min 为最佳。 关键词：热压含碳球团；水分；粒度；加热时间；强度 Study on the influence factors of the strength of Carbon Composite Iron Ore Hot Briquette LI Jun, JI Qiang, LI Peng (School of Chemical and Environment Engineering, China University ofMining and Technology (Beijing ), Beijing 100083) Abstract: Focus on the impact of different moisture content, particle size and heating time of Raw material on the strength of the carbon composite iron ore hot briquette (CCB), and to explore the mechanism of pellet strength. The experimental results show that Raw moisture content has little influence on the pellet strength. Coal, ore particle size have a great influence on the pellet strength, when the coal 0.18mm, the mine 0.45mm ,the pellet strength is 270kg each. Heating time has a great influence on the pellet strength, within this experimental conditions the best heating time is 30 min. Keywords: carbon composite iron ore hot briquette (CCB); moisture content; particle size; strength; heating time 0 引言 高炉炼铁是钢铁生产中重要环节, 降低高炉燃料比和焦比一直作为高炉炼铁节能的主 要措施，而降低燃料比和提高喷煤比的主要途径为提高布料控制水平和操作水平，这种传统 的高炉技术已发展到日臻完善的水平。另外原燃料条件不断恶化，富矿资源减少，使高炉负 担加重，冶炼指标下降。在全球对节能减排要求日趋严格的形势下, 急需开发创新型的能够 大力节能和减少污染物排放的新型炉料。因此,一些低温炼铁技术成为炼铁工作者的研究热 点。[1,2] 热压含碳球团是将矿粉和煤粉混合后加热到一定温度，煤加热时产生的胶质体作为黏结 剂，在一定压力下压制而成的为热压团块。热压含碳球团作为一种新型炼铁炉料成为人们研 究的热点，储满生等对煤种及热压工艺参数等进行了系统的研究。[3,4]本研究主要对物料水 分、粒度、加热时间等进行了研究。 1 实验 1.1 实验材料 实验中所用铁矿粉、肥煤主要成分及特性如表 1 和表 2 。