82B洁净度控制研究.pdfVIP

2013 年 9 月 2013 年特钢年会论文集 Sept. 2013 82B 洁净度控制研究 闫卫兵 （河北钢铁集团宣钢公司（河北省钢结构用钢工程技术研究中心），河北，张家口，075100 ） 摘 要：宣钢生产的 82B 盘条存在拉拔脆断，主要原因是盘条中存在大尺寸的非金属夹杂物和心部网状碳 化物，采用示踪剂跟踪、系统取样和实验室分析相结合的方式，对 82B 生产全流程各个工序环节进行系统 取样，分析各工序钢中 T[O]和[N]、夹杂物的数量、大小、组成和类型以及来源和变化规律，并和国内外相 同工艺先进厂家的洁净度控制水平进行对比，找到了影响铸坯洁净度的限制性环节，并制定有针对性的工 艺改进措施，使 82B 洁净度大幅改观。 关键词：82B 盘条，洁净度，夹杂物，T[O]和[N] Study on Purity Control of 82B Yan Weibin (Hebei Iron ＆Steel Group Xuanhua Iron ＆Steel Co., Ltd., Zhang Jiakou Hebei Province 075100) Abstract: 82B wire rod produced by Xuanhua Steel has the problem of drawing brittle fracture, the main reason is non-metallic inclusion throughout and network carbide in center. We found influence factors of casting purity by taking some methods, such as using tracer, sampling through the whole production process of 82B and experimental analysis of T[O]和[N], the number , size , form and type of inclusions, and finding the sources and changes, as well as making comparison with other advanced company who has the same technology and made relevant improved steps with improved 82B purity. Key words: 82B wire rod, purity, inclusion, T[O] and [N] 1. 前言 82B 盘条是宣钢近年来开发的品种线材，主要用于生产建筑和交通运输行业广泛使用的 高强度预应力钢丝和钢绞线。为了获得高质量线材，对铸坯质量提出了严格的要求，要求铸 [1] 坯夹杂物少、夹杂物粒径小、中心碳偏析小、表面质量好 。因此，82B 钢具有较高的生产 难度。目前，宣钢高碳钢盘条的质量异议主要是拉拔脆断，断口多呈笔尖状。通过对断口形 貌、组织和成分的分析，发现造成高碳钢盘条拉拔脆断的主要原因是盘条中存在大尺寸的非 金属夹杂物和心部网状碳化物。非金属夹杂物的存在是影响钢丝拉拔性能的主要因素之一。 非金属夹杂物的危害在于它们在钢中呈独立相存在，破坏了钢基体的均匀连续性，造成应力 集中，促使裂纹产生，并在一定条件下加速了裂纹的扩展，从而导致钢丝拉拔断裂。为了提 高高碳钢的洁净度，进一步改善高碳钢硬线的拉拔性能，宣钢以 82B 生产工艺为基础对高 碳钢洁净度进行了系统的研究和工艺改进。 185 2013 年 9 月 2013 年特钢年会论文集 Sept. 2013 2. 82B 洁净度研究 2.1 工艺流程 宣钢高碳钢方坯生产的工艺流程是：铁水预脱硫→110t 转炉→110t 钢包炉精炼→