基于N-异丙基丙烯酰胺温敏型分子印迹聚合物.pdfVIP

《化学通报》在线预览版 基于N-异丙基丙烯酰胺的温敏型分子印迹聚合物 * 夏烈文 褚良银 (四川大学化工学院 成都 610065) 摘 要 温敏型分子印迹技术是近几年来分子印迹技术新的发展。温敏型分子印迹聚合物以低交联度为特征，对模板 分子的吸附容量和选择性随温度变化而改变。本文总结并评述了基于 N-异丙基丙烯酰胺的温敏型 MIP 分子印迹聚合物及 其制备方法，指出了温敏型分子印迹技术发展中需要解决的问题。 关键词：分子印迹；N-异丙基丙烯酰胺；温度敏感 Temperature-sensitive Molecular Imprinted polymers Based on N-isopropylacrylamide Xia Liewen, Chu Liangyin* ( School of Chemical Engineering, Sichuan University, Chengdu 610065) Abstract Temperature-sensitive molecular imprinting is a new branch coming into being in recent years. Temperature-sensitive molecularly imprinted polymer is featured with its low rate cross-linkage and the responsive binding capacity and selectivity to template molecules according to surrounding temperature. In this paper the temperature-sensitive molecularly imprinted polymers based on N-isopropylacrylamide are reviewed, and the current problems in developing temperature-sensitive molecular imprinting technology are also pointed out. Key words Molecular imprinting, N-isopropylacrylamide, Temperature-sensitive 分子印迹技术起源于 20 世纪 40~50 年代根据鲍林关于用抗原来制备抗体的理论用硅胶制备吸附染 料的材料[1~3]，但是是在 70 年代 G. Wulff 和 80 年代 K. Mosbach 开创了以高分子聚合物与模板分子（也 叫印迹分子）以共价或非共价方式作用来制备分子印迹聚合物（MIP ）之后，分子印迹技术才开始得到 人们的关注[4,5] 。由于分子印迹技术具有构效预定性、特异识别性和广泛实用性而得到大量研究，特别是 90 年代以来，分子印迹技术的研究开发机构、研究人员和报道的成果数量每年呈几何级数的增长[6] 。国 内对分子印迹技术的研究在 2000 年后得到了较快的发展，成果报道数量稳步增长。MIP 识别模板分子 的能力是基于聚合物中功能单体能按特定的空间位置分布并与模板分子中相应的基团发生静电、氢键、 偶极或疏水等相互作用。因此，MIP 对模板分子的特异性识别要求印迹空腔具有一定的形状和大小，如 同酶和底物按“锁-钥”模式进行识别一样。这就要求 MIP 具有一定的刚性以维持印迹空腔的形状和尺 寸的稳定，因此不得不采用很高的交联度[7~9] 。高交联度高分子材料往往具有质硬易碎的性质，高交联 度也使得模板分子在 MIP 中传质速度慢，使模板分子的洗脱和再结合困难。利用一些高分子的柔性和温 敏特性可以改善高交联度 MIP 的上述缺点。同时，温敏特性的引入使 MI