60Si2CrVA弹簧钢力学性能影响因素的研究.pdfVIP

60Si CrVA 弹簧钢力学性能影响因素研究 2 林 宪 郭昭桥 林水石 余其中 （杭州钢铁集团公司技术中心，杭州 310022 ） 摘 要 研究了获得60Si CrVA 弹簧钢良好综合力学性能的较为合适的热处理工艺。进行了压缩比对力学性能的影 2 响试验。采用显微硬度、金相组织及扫描电镜能谱分析等方法，结果表明：组织不均匀是导致钢材力学性能不合格 的主要因素之一。并指出了改进措施和建议。 关键词 60Si2CrVA 弹簧钢 力学性能 热处理工艺 压缩比 金相组织 Study on Factors Effecting Mechanical Properties of 60Si CrVA 2 Spring Steel Lin Xian Guo Zhaoqiao Lin Shuishi Yu Qizhong (Hangzhou Iron and Steel Group Corporation ，Technology Center ，Hangzhou ，310022) Abstract Heat threatment process was studied ,which can gain compositive mechanical properties of 60Si CrVA spring 2 steel.The test on compression ratio affecting mechanical properties was implemented.Some kind of study means are used ,for example,microhardness,metallographic structure, SEM and EDS analysis .The result shows that uneven structure is one of the major factors causing unsound mechanical properties, remedy measures and advices are pointed out. Key words 60Si2CrVA spring steel, mechanical properties, heat threatment process, compression ratio, metallographic structure 1 引言 60Si CrVA 弹簧钢主要用于制造铁道、电力、工程机械等行业用弹簧，其质量要求高，市场容量大，附 2 加值较高。杭州钢铁集团公司根据市场需求和多年来生产弹簧钢的经验，2007 年始开发此品种。从 4 月份 至 7 月份小批量试产了φ 8mm、φ11mm 的高速线材 60Si2CrVA 弹簧钢和φ18mm 至φ46mm 范围内各种规格的 60Si2CrVA 棒材。采用的工艺为：EAF （结晶器电磁搅拌）+LF+VD+CCM ，150×150mm 连铸坯轧钢一火成 材。 从产品质量检验情况来看，低倍检验：一般疏松、中心疏松及偏析均不超过2.0 级；非金属夹杂检验： A 、B、C 类夹杂物均小于2.0 级，D 类夹杂物小于 1.5 级；总脱碳层深度不大于直径的 1.0％；顶锻试验结 果完好。这些检验项目均能满足用户要求。但在对力学性能的检验过程中，发现该钢种对热处理工艺参数的 变化非常敏感，合适的工艺参数范围较窄。有些规格的产品按常规方法进行热处理，力