梅山连铸中间包水模拟试验研究.docVIP

梅山连铸中间包水模拟试验研究 刘　欢　韩孝永* 　　摘　要　进行了中间包挡墙和坝的水模拟优化试验,确定出挡墙和坝的最佳设计方案,同时与重庆钢铁设计院设计的中间包挡墙和坝的方案进行水模拟对比试验,分析了各自的流场特点，最后指出本试验最佳设计方案为梅山中间包挡墙和坝的理想设计方案。　　关键词　连铸中间包　水模拟试验　理想设计方案 Research on Tundish Water Simulation Experiment in Meishan Co.Ltd Liu Huan　Han Xiaoyong(Meishan Co.Ltd of Shanghai Corp.) Abstract　By water simulation experiments on tundish dam and weir, the optimal design of dam and weir has been determined, Which is compared with the design made by Chongqing Iron Steel Design Institute throguh water simulation experiments. The characteristics of flow fields of both desing plans have Been Individually analyzed. Finally it is put forward that the design of tundish dam and weir made by Meishan Corporation is the best ideal design.Keywords　continuous casting tundish　water simulation experiment　ideal design plan 1　前言 　　重庆钢铁设计院为梅山炼钢连铸提供了中间包挡墙和坝控制流参数的设计数据,但未进行水模拟试验研究。因此,开展中间包水模拟试验研究,优化中间包挡墙和坝的控制流参数,为梅山连铸生产提供中间包最佳挡墙和坝的尺寸与位置,以便在中间包内创造一个良好的使夹杂物上浮而不卷入钢水的条件,这对净化钢水、提高连铸板坯质量有直接的经济效益和社会效益。 2　试验原理和方案 　　水模拟试验的理论基础是相似原理,即模型与实型中液体流动相似的基本条件是几何相似和动力相似。对于几何相似,可以采用任何比例,根据国内外文献报导和试验实际条件,模型(Lm)与实型(LR)的几何相似比例选择Lm:LR=1:4。对于动力相似要求模型与实型中的流体的雷诺准数Re和弗鲁德准数Fr分别相等,才能保证动力相似,但满足模型与实型中的两个相似准数同时相等相当困难,考虑到在此试验条件下,模型与实型中的流体流动状态均已处于第二自模化区,因此,该系统的流动状态及流速分布与雷诺准数Re无关,只要求保证与重力有关的弗鲁德准数Fr相等即可达到动力相似。　　由Fr准数相等可以确定模型与实型中流体的速度、流量、平均停留时间的关系。　　由Frm=FrR即: 　　得速度比: 　　流量比: 　　平均停留时间比: 式中　下标m代表模型,下标R代表实型　　　g——重力加速度　　　L——特征长度　　　V——流体速度　　　Q——流体流量　　　——流体平均停留时间　　对于中间包控制流参数的设计,参考了国内外有关中间包挡墙和坝的研究和应用数据,采用L9(34)正交试验方案表,确定了9组中间包控制流试验数据,根据试验测定流体实际平均停留时间的长短和死区大小,效果最佳的那一组,即为中间包挡墙和坝的最佳联合设计方案。中间包流场正交试验方案如表1所示。 表1　中间包流场试验方案 试验号 a/mm b/mm c/mm d/mm 1 700(175) 270(67.5) 150(37.5) 300(75) 2 700(175) 410(102.5) 200(50) 400(100) 3 700(175) 550(137.5) 250(62.5) 500(125) 4 900(225) 270(67.5) 200(50) 500(125) 5 900(225) 410(102.5) 250(62.5) 300(75) 6 900(225) 550(137.5) 150(37.5) 400(100) 7 1100(275) 270(67.5) 250(62.5) 400(100) 8 1100(275) 410(102.5) 150(37.5) 500(125) 9 1100(275) 550(137.5) 200(50) 300(75) 注:表中括号外为原型数据,括号