减缩剂和水泥适应性的研究.pdfVIP

减缩剂与水泥适应性的研究 张志宾，徐玲玲，刘方，杨静，章明 （南京工业大学材料学院，南京210009 ） 摘 要：本文通过比较减缩剂对硅酸盐水泥、粉煤灰水泥、煤矸石水泥和复合水泥净浆自收 缩的减缩效果，研究了减缩剂与水泥的适应性。结果表明：减缩剂与水泥有较好的适应性。 并讨论了影响减缩剂与水泥适应性的因素：水泥的矿物组成和细度、混合材的种类、水泥的 碱含量等。 关键词：减缩剂 自收缩 适应性 中图分类号：TQ172.4+6 Study of Compatibility Between Shrinkage Reducing Agent and Cement ZHANG Zhibin, XU Lingling, Liu Fang, Yang Jing, Zhang Min (College of Material Science and Engineering，Nanjing University of Technology ，Nanjing 210009,China) Abstract: In this paper the compatibility between SRA and cement is studied by comparing the shrinkage reducing effect of shrinkage reducing agent (SRA) in neat cement, fly ash cement, coal-gangue cement and blended cement paste respectively. Experiment results show that SRA and cement has better compatibility. In addition, such factors as mineral compositions and fineness of cement, type of cement admixtures and alkali content of cement is discussed in terms of effect on compatibility. Key words: SRA; Autogenous shrinkage; Compatibility 近年来高性能混凝土在高层建筑、大跨桥梁、海上建筑和高速公路等建设中使用愈来愈 普遍，由于高效减水剂和矿物质超细粉掺合料等的使用，高性能混凝土的自收缩和干燥收缩 值增加，早期尤为明显。收缩值增大必然引起混凝土开裂的几率增加。混凝土的收缩裂缝问 题一直困扰着材料和工程界。国内外采取了各种各样的方法来减小收缩，如在混凝土搅拌时 [1] [2] [3-5] 掺入膨胀剂 、纤维 、减缩剂 和改善养护条件等。由于减缩剂在减少混凝土的自收缩和 干燥收缩方面的突出作用，著名的学者S P SHAH把混凝土减缩剂列为预防混凝土收缩开裂 第一作者：张志宾（1981～），男，博士研究生，E-mail: zhangnjut@163.com 通讯作者：徐玲玲（1964～），博士，教授，水泥物理化学，E-mail: XLL@ [6] 的两个措施(纤维增强和混凝土减缩剂)之一 。日本早在20 世纪 80 年代就开始从事减缩剂 的研究，第一种减缩剂于 1982 年由日产水泥株式会社和三洋化工株式会社研制成功，并于 1982 年取得专利[7] 。随后，日本和美国的众多学者对这一领域进行了广泛深入的研究，产品 在厂房、道路、桥梁、隧道、水池和堤岸等许多工程中加以应用，取得了较好的效果。我国 关于减缩剂的研究和报导始于 20 世纪 90 年代，由于减缩剂的成本较高，一直没有得到推广 应用。但随着混凝土工程裂缝控制的迫切需要，以及减缩剂研究技术和产品性能的进一步提 高，减缩剂这一新型水泥基材料外加剂定将得到越来越广泛的应用。近年来对减缩剂性能的 研究很多，重点在减缩性能和对水泥基材料强度的影响