KNaRE复合变质在增碳法生产球铁中的作用.pdfVIP

K/Na-RE 复合变质在增碳法生产球铁中的作用 谢瑞财，杨华，焦金玲 （山东大学材料液态结构及其遗传性教育部重点实验室，山东 济南 250061 ） 摘要：本文研究了采用增碳工艺法生产球墨铸铁时 K/Na-RE 复合变质处理的作用，发现： 合理使用 K/Na-RE 复合变质剂能够优化增碳处理工艺，改善铁液质量，显著提高铁液的石 墨形核状态，从而增加石墨球的数量，细化石墨球和基体组织。 关键词：球墨铸铁，增碳工艺，K/Na-RE 复合变质 中图分类号：TG143.5 EFFECT OF K/NA-RE MULTIPLE MODIFICATION ON NODULAR IRON PRODUCED BY THE RECARBURATION PROCESS XIE Rui-cai, YANG Hua，JIAO Jin-ling （Key Laboratory of Liquid Structure and Heredity of Materials, Ministry of Education, Shandong University, Jinan 250061,Shandong,China ） Abstract : In this paper, the effect of the K/Na-RE modification added into nodular cast iron that was produced by the recarburation process was investigated. The results indicate that K/Na-RE has an excellent effect on the recarburation process. It can increase the melt quality and nucleation state remarkably. As a result, the nodule amount has an obvious increase and the nodules became fine and homogeneous. Keywords: nodular iron, recarburation process, K/Na-RE multiple modification 在球墨铸铁的生产中，使用增碳剂对铁液进行增碳处理，可以在铁液中生成 大量弥散分布的非均质结晶核心，降低铁液的过冷度，从而有利于石墨的形核， 增加石墨球的数量，并且采用废钢加生铁通过增碳处理生产球铁，既能节省大量 优质生铁，降低成本，又能提高铸件性能，所以球铁的增碳工艺研究越来越得到 大家的重视[1]。 作 者 简 介 ： 谢 瑞 财 （ 1982- ）， 男 ， 山 东 济 南 人 ， 在 读 硕 士 ， 主 要 从 事 球 墨 铸 铁 研 究 ， E-mail :kaige@mail.sdu.edu.cn, 电话：0531 但是，迄今国内外对球铁增碳工艺的研究报道较少。在实际增碳过程中，增 碳效果较差，且不易控制[1]。因此，研究如何优化增碳处理工艺，稳定增碳效果， 从而进一步提高球铁的性能具有非常重要的现实意义。本文主要研究了在增碳处 理过程中，K/Na-RE复合变质剂的影响，并对其机理进行的初步探讨。 1 材料及试验方法 1.1 化学成分的选择 [2] 球铁的化学成分与最终铸件的组织，性能都有极大的关系 ，合适的化学成 分是获得优质铸件的前提。为了获得高强韧的球墨铸铁，结合实际生产需要，制 定出表 1 所示的化学成分。 表 1 铁液的化学成分 w % ｂ Table1 Composition control range of molten iron （w %）