600MPa级冷轧双相钢地连续冷却转变研究.pdfVIP

2007 中国钢铁年会论文集 600MPa 级冷轧双相钢的连续冷却转变研究 李激光 鲁 月 （辽宁科技大学材料科学与工程学院，鞍山 114051 ） 摘 要 采用热模拟试验研究了低C-Si-Mn 系双相钢的过冷奥氏体连续冷却转变规律，对不同冷却速率下试验钢的 显微组织构成进行了定量分析，分析了连续冷却曲线对退火工艺参数的影响。为制定最佳退火工艺、获得良好组织 状态和综合力学性能提供理论指导。 关键词 冷轧双相钢 连续冷却 过时效 微观组织 Research on the Continuous Cooling Transformation Laws of DP600 MPa Steel under Cool Rolling Li Jiguang Lu Yue （School of Materials Science and Engineering, University of Science and Technology Liaoning, Anshan, 114051 ） Abstract The continuous cooling transformation laws of overcooling austenite of low C-Si-Mn dual phase(DP) steel were researched by thermal simulation machine, quantitative analysis were carried on the microstructures of DP steel at deferent cooling rates, the effects of continuous cooling curve of DP steel on annealing processing parameters. This will offer a guide for determining optimal annealing processing, gaining better microstructures and combination mechanical properties. Key words cold rolling dual phase steel, continuous cooling, overaging, microstructures 随着汽车工业对安全与节能的要求，减轻汽车自重，提高构件强度成为汽车选材的关键，因而成形性良 好的高强度钢板成为汽车用钢的首选。双相钢以其低屈强比，高抗拉强度，良好的均匀延伸率，高的加工硬 化速率等特点，已发展成为汽车用高强钢的主体[1～4] 。冷轧双相钢的生产要经过冶炼、热轧、冷轧与连续退 火等过程，双相钢的组织主要由铁素体与马氏体组成，为保证所生产的双相钢具有合理比例的双相组织，本 文研究了双相钢的相变规律，为热轧冷却以及连续退火工艺参数的制定提供重要的试验数据。 1 试验材料与方法 1.1 试验材料 试验钢的成分选取低碳-Si-Mn 系列，将设计好的钢种在实验室200kg 真空感应炉中冶炼并浇注成钢锭， 然后将钢锭热轧成20mm 厚的中间坯料，累计压下为77 ％，将中间坯加工成φ6×15 的热模拟圆柱试样。由 于热轧过程经历了奥氏体化相变、动态再结晶、铁素体珠光体相变，因此坯料组织成分比铸态组织均匀。 1.2 试验方法 按照图 1 所示的工艺方案在 Gleeble-1500 热模拟机上进行试验。试样以 10℃/s 的速度加热到 950℃保温 5min 完全奥氏体化后，再以5℃/s 的速度冷却到850℃，保温30s 后，以不同的冷却速度（0.3℃/s 、1℃/s 、 2 ℃/s 、3℃/s 、5℃/s 、8℃/s 、15℃/s 、25 ℃/s 、40 ℃/s 、60℃/s ）冷却到室温以测定DP600 双相钢的静态连续 冷却曲线