(6) 高分子材料 交联型PVC/TPU 轻质材料及其制备方法 2 1 焦雷，陈聪，陈程，王伟，刘艺舟，郭卫红 (华东理工大学材料科学与工程学院高分子合金研究室,上海,200237) 摘 要：以PVC,TPU 为主要原料，加入交联剂DCP ，发泡剂AC 及其他助剂经模压成型制备了PVC/TPU 轻质材料。通过冲击测试、抗弯测试、拉伸测试以及密度测试研究了TPU 用量、DCP 用量对PVC/TPU 发 泡材料力学性能的影响，用红外光谱研究材料基团的变化，用 SEM 扫描电镜表征了材料的泡孔形状、尺寸 以及排列。 关键词：聚氯乙烯；热塑性聚氨酯；发泡 Study on preparation of cross-linked PVC/TPU lightweight materials 1 JIAO Lei , CHEN Cong, CHEN Chen, WANG Wei, LIU Yizhou, GUO Weihong2 (Polymer Alloy Lab, East China University of Science and Technology, Shanghai 200237) Abstract: The crosslinked PVC/TPU lightweight materials were prepared by sheet molding method. DCP was incoperated as crosslinking agent and AC as foaming agent. The effect s of the composition ratio of PVC/TPU and the content of DCP on PVC/TPU lightweight materials were studied by impact test, tensile test , bending test and density test. Besides, the reactions of DCP and PVC as well as DCP and TPU were studied by IR. Bubble quality, size, and the topology were studied by SEM. Key words: PVC, TPU, foaming 0 引言 聚合物发泡材料是指以聚合物为基础而其内部具有无数气泡的微孔材料，也可视为以气 体为填料的复合材料。 硬质聚氯乙烯(RPVC)发泡板材是一种新型材料，广泛用于建材、广告等行业。它质轻、 难燃、防水、防腐、绝缘，并且具有良好的隔音、隔热性能。不仅可以像木材一样进行切割、 锯、钉、铣、刨加工，而且可以进行焊接、黏接、丝网印刷、电镀、烫印等深加工。在力图 保护森林资源，环保意识越来越强的今天，开发硬质聚氯乙烯发泡材料意义重大。但其硬制 品抗冲击性能差，易脆裂，同时增塑剂易迁移，使材料的性能下降。所以对PVC 材料的增 韧一直是开发PVC 材料的主要方向。对于聚烯烃类聚合物，一般需要使熔融树脂在发泡之 前做适当的交联处理，由线型结构转变成体型网状结构，从而调整树脂的粘弹性，以适应发 泡要求。另一方面，通过交联发泡工艺还可提高泡沫塑料的耐热性和力学性能。聚氯乙烯泡 沫材料是泡沫塑料中重要的品种之一。对PVC 进行交联改性是一种提高PVC 泡沫材料的耐 热性、耐溶剂性、抗压缩变形及生产工艺等性能的重要途径。 热塑性聚氨酯(TPU)是一种新型的热塑性弹性体，可用作 PVC 的增韧剂，具有极好的 耐腐蚀性、耐油性、耐寒性及高的拉伸强度和伸长率。同时在增韧PVC 材料的同时，还可 1基金项目：国家科技支撑计划重点项目（2008BAC46B 10），西南科技大学生物质材料教育部工程研究中 心的开放基金的资助(2010) 以及全国大学生创新计划(101025122) 。焦雷，男，陕西省咸阳市人，在读研究 生，主要从事PVC 成型加工及硬质P