高炉冷却水质结垢及研究设计选择.pdfVIP

高炉冷却水质的结垢研究与设计选择 ·1 · 高炉冷却水质的结垢研究与设计选择 胡源申 （安徽工业大学，马鞍山 243002 ） 摘 要 为抑制高炉冷却壁内水管的结垢，使用某钢二铁和四铁厂高炉现场不同冷却水质进行了实验室模拟结垢研 究。采用数码摄相、扫描电镜、化学分析、称重测试、X 射线衍射相分析等方法，考察了冷却水质、水管材质、水 中溶氧等因素对结垢的影响及其一般规律。根据实验结果，提出了缓结垢的一些工业实施对策与设计选择建议。 关键词 高炉 冷却水 冷却壁 结垢 Study on Scale Formation of Water Pipe in BF Cooling Stave and Industry Measures Refraining Scale Formation Hu Yuanshen (Anhui University of Technology，Maanshan ，243002) Abstract In order to restrain incrustation of water pipe in BF cooling stave,by means of digit pictures, SEM analysis, chemistry analysis, weight change test and X-ray phase analysis ,a modeled scale formation study has been made on BF cooling water of No.2 and No.4 Ironmaking plant at Maanshan Iron and Steel Co.,Ltd.. This article discussed quality of cooling water, material of water pipe, oxygen content in water and its effect on the cooling water incrustation, as well as the normal law of scale formation. According to the experiment results, some proposals and industry measures refraining to scale formation are discussed and put forward. Key words blast furnace, cooling water, cooling stave, scale formation 1 前言 国内外高炉的生产实践证明，高炉本体及其附属设备即使是在高效化生产的背景下，一般也能达到 20 年左右的寿命，而高炉的冷却器，尤其是我国大多数高炉现在较多采用的冷却壁一般却只有4~6 年的使用寿 命。因此高效化与长寿化之间出现了突出的矛盾，高炉长寿已越来越依赖于冷却壁寿命的提高。 对破损冷却壁进行的解剖研究发现，冷却水在冷却壁内水管上的结垢是影响冷却壁寿命的一个极其重要 的因素。以球铁材质冷却壁为例，其壁内水管水垢的导热系数测得在1.6~1.8w/mk，而材质的导热系数则在 29.1~34.9 w/mk ，水垢的导热系数仅为壁体的1/24~1/30。根据实验，形成1mm 厚的垢，冷却壁的换热量会 下降80%左右，将对冷却壁造成50~100℃的温升。因此高炉中晚期因冷却壁内水管结垢已逐渐增厚会使热 [1] 阻越来越大，实际过水量减小带走热减少，极易