辐射研究与辐射工艺学报990302 辐射研究与辐射工艺学报 JOURNAL OF RADIATION RESEARCH AND RADIATION PROCESSING 1999年 第17卷 第3期Vol.17 No.3 1999 硅橡胶膜上NIPAAm预辐射接枝机理研究 李　军　伊　敏　卢　君　高宏成　哈鸿飞 　　摘要　采用预辐射方式将NIPAAm接枝到硅橡胶上,结果表明:接枝反 应是由样品在 空气中辐照生成的过氧化物(主要是氢 过氧化物)引发的,并且仅在较高温度下接枝才能 进行。研究了过氧化物的产生和分解, 计算出过氧化物分解的活化能为27.2kJ/mol。通过 对接枝反应动力学的研究表明,接枝反 应的活化能较低,约54.7kJ/mol。讨论了接枝反应机 理。 　　关键词　硅橡胶,氮-异丙 基丙烯酰胺,预辐射接枝,温度敏感性聚合物,过氧化物 STUDY ON PRE-IRRADIATION GRAFTING MECHANISM OF NIPAAM ONTO SILICONE RUBBER LI Jun　 YI Min　LU Jun　 GAO Hongcheng　HA Hongfei (Department of Technical Physics, Peking University, Beijing 100871) 　　ABSTRACT　Pre-irradiation grafting of polyNIPAAm on silicone rubber was completed successfully. It was found that the graftaction could be done just at higher temperature and induced by peroxides (mainly hydrogen peroxides) produced during irradiation of samples in air. Production and decomposition of the peroxides were investigated. The active energy of peroxides decomposition equals to 27.2 kJ/mol. The study of grafting kinetics showed that the graftaction is easy to occur at higher temperature because of the active energy of graftaction was low, near to 54.7kJ/mol. And the grafting mechanism was discussed deeply. 　　KEYWORDS　Silicone rubber, NIPAAm, Pre-irradiation grafting, Thermo-sensitive polymer, Peroxides 的接枝是令人感兴趣的课 题,因为这可应用于生物活性物质的固定,生物分子的分离和药 物缓释体系 [2～4] [5] 。目前 在文献中能找到几篇此体系共辐射接枝的文章 ,但极少发现此 体系预辐射接枝 研究。 作为一种很柔顺的生物材料,硅橡胶可以广泛地用作辐射接枝的 [6,7] 基材 。 在空气中 辐照后,几乎所有生成的自由基与氧气结合而生成过氧化物。因为 过氧化物的分解一般 需要较高的温度,所以在室温下接枝反应难以进行。 本文较深入地 研究了NIPAAm在硅橡 胶上的预辐射接枝和过氧化物的生成、分解。 file:///E|/qk/fsyjyfsgyxb/fsyj99/fsyj9903/990302.htm（第 1／7 页）2010-3-22 19:08:12 辐射研究与辐射工艺学报990302