铬渣在青钢烧结生产中的应用实践.docVIP

铬渣在青钢烧结生产中的应用实践 王东 （山东省，青岛市，266043） 摘要：铬渣是社会公认的有害工业废渣;青钢烧结通过技术改造，以铬渣代替部分熔剂，完成了青岛市存贮数十年，总量达20余万吨铬渣消化任务；铬渣消化过程中代替部分白云石和生石灰，其固有的粘性改善了混合料的制粒效果，促进了烧结生产的顺利进行；同时周边居民生活环境得带显著改善，逐步降低地下水污染的危害，带来巨大经济效益和社会效益。 关键字：铬渣 熔剂 污染 烧结矿 环保 Ore sintering with the Chromium slag addition at Qingdao Iron and Steel co. Ltd WangDong (Qingdao Iron and Steel, Ltd , Qingdao266043, Shandong) Abstract: The Chromium Slag is a harmful waste slag approved by ereryone; Qinggang sinter plant have completed the task of adding more than 200000 tons Chromium Slag storaged many years at Qingdao，through replaced art of flux by the Chromium Slag. In the digestion process, the Chromium Slag had improved the effect of granulating with the mixture and promoted the sintering process because of it’s unique adhesion. At the same time, people’s living environment have been improved, underground water become more and more secure, the item bring a lot of effectiveness of Economic and Social. Key words: The Chromium Slag flux poisonousness sinter environmental protection 1、前言 铬盐广泛应用于国民经济的各个领域而且大多数是必不可少的消耗性化工原料。每生产1 吨铬盐产品会产生2.5～3 吨铬渣。铬渣中因含有1～2%的具有致癌特性的铬酸钙和0.5～1%水溶性剧毒而成为有毒的危险废物。表1 铬渣化学成分表 化学成分 Tfe SiO2 CaO MgO Al2O3 水分 烧损 含量 6.89 10.89 27.53 19.24 4.82 7.5 23.5 3、技术方案 3.1工艺原理 铬渣在烧结工艺中的还原解毒机理：铬渣中的Cr6+在烧结高温、还原气氛下被还原成Cr3+,其主要反应有: 2Na2CrO4+3CO△Cr2O3+2Na2O+3CO2 (1) 2CaCrO4+3CO△Cr2O3+2CaO+3CO2 (2) 2CrO3+3CO△Cr2O3+3CaO (3) 铬渣经高温熔融,形成新的液相,经降温、结晶、冷却、固结,把未还原的Cr6+和已还原的Cr3+固封在烧结矿中。 铬渣在炼铁工艺中的还原解毒机理：高炉炉膛中高温下的C和CO具有强烈的还原性,使Cr6+和Cr3+进一步得到还原,主要反应除上述(1)、(2)、(3)外,还有如下(4)、(5)反应: Cr2O3+3C△2Cr+3CO (4) Cr2O3+3COΔ2Cr+3CO2 (5) Cr6+可被还原为低毒的Cr3+,并进一步还原为无毒的单质Cr,进入铁水中。 3.2配比方案 铬渣系化工厂以铬盐制成红矾钠后的废弃渣,其中含有较高的CaO和MgO,可以作为烧结熔剂配料,取代部分消石灰和白云石。铬渣在实际生产组织过程中，以一种熔剂参与配料作业，其化学成分见表1。各物料化学成分见表2，配比结构见表3表2 各物料化学成分表（%） 物料名称 TFe SiO2 CaO MgO Al2O3 水分 烧损 混合料 59.65 4.82 3.45 1.62 1.58 5.89 3.79 焦粉 9.00 1.50 5.00 9.5 78 生石灰 6.09 80.00 1.42 0.71 0 15.1 白云石 5.13 31.00 19.00 1 43 表3 烧结配比结