环保型无碳水基转炉大面自流料的开发及应用 董战春 邓乐锐 章荣会 （北京联合荣大工程材料有限责任公司，北京 101400 ） 摘 要 本文通过分散剂的筛选，确定出最适合环保型无碳水基转炉大面自流修补料的分散剂及其加入量。而后在 此基础上依据安德烈森理论，制定出一最佳配比方案。最后对该方案常规物理性能、高温自流性及烧结时间等进测 定，并与传统转炉大面自流修补料性能进行了对比，发现其性能优于传统转炉大面自流修补料，最为重要的是其提 供了一个无烟尘无毒气危害的现场施工环境。 关键词 转炉 无碳 环保 Environmental Protection No Carbon Self-flow Fefractory for Converter Bedding Face Development and Application Dong Zhanchun Deng Lerui Zhang Ronghui (Beijing Allied Rongda Engineering Material Co., Ltd., Beijing, 101400) Abstract This article through the screening of the dispersant, to determine the most suitable for the environment-friendly no carbon water-based repairing materials for converter bedding face their dispersant and added amount. And then based on this basis, make a theorys Andre a the best proportion plan. Finally the scheme for regular physical performance, high temperature sintering and sexual and their time was determined, and with the traditional repairing materials for converter bedding face their performance were compared. The performance is better than that of traditional found their repairing materials for converter bedding face, the most important is its provides a no smoke without gas of the harm of site construction environment. Key words converter,no carbon,environmental 1 引言 目前随着我国钢铁行业持续的整合和迅速发展，钢铁企业的再扩大生产与所面临的环保、能源和社会关 系的协调就逐渐成为一个关键性的问题。 转炉处在炼钢生产流程的中心，是钢厂的主要设备之一。转炉的装料侧、出钢侧和炉底的耐火材料长期 处在高温状态下，并受到机械力冲击和炉渣的反复侵蚀,其结构极易遭到破坏。目前，国内外的大多数转炉 每炼钢8～10 炉次就必须进行炉底和大面修补[1] 。 用于转炉大面修补的传统材料结合系统分为：有机结合和无机结合。无机结合的修补料具有流动性好、 挥发分少及较短的硬化时间，但由于低熔点无机盐的加入，致使寿命不高难以满足使用要求。因此，目前现 场修补所使用的转炉大面修补料，主要以煤焦油、沥青（约8%～15%）、树脂等有机物质作为结合剂。其中 沥青系的流动性较好；树脂的抗渣侵蚀性能优良，现场工人操作简便，补炉