p-Fe日纳米线的制备及表征.docVIP

p-Fe00日纳米线的制备及表征 2005年第63卷 第11期化学学报 ACTH CHIMICA SINICA Vol. 63, 2005 No. 11.·研究简报。 p-Fe00日纳米线的制备及表征 王晓娟 蒋晓红 郭新勇 王洪哲 张兴堂 李蕴才 杜祖亮* (河南大学特种功能材料重点实验室开封475001) 摘要通过无机铁(III)盐的水解在常温条件下制备了(3-Fe00H纳米线，并用透射电子显微镜(TEM)、高分辨透射电镜 (HRTEM). X射线衍射(XRD)及选区电子衍射((SHED)对其形貌及结构进行了表征.电镜结果表明，所得到的纳米线直 径约60 nn，长度为4-V5 pm，且沿[001]方向生长.XRD结果表明纳米线为四方相(3-Fe00H，在常温下结晶性良好.研 究表明FeC13浓度对纳米线生长有很大影响，只有当FeC13浓度合适时，才能制备出高质量的纳米线. 关键词(D-Fe00H;纳米线;水解 Preparation and Characterization ofp一Fe00H Nanowires WANG, Xiao-Juan JIANG, Xiao-Hong WANG, Hong-Zhe ZHANG, Xing-Tang LI GUO, Xin-Yong Yun-Cai DU, Zu-Liang* (Key Laboratory of Special Function Materials, Henan University, Kaifeng 475001) Abstractp-Fe00H nanowires were synthesized via hydrolysis of iron(III) salts under room temperature. The morphology and structure were characterized by transmission electron microscopy, high-resolution transmission electron microscopy, X-ray diffraction, and selected area electron diffraction. The results showed that the nanowires were tetragonal lattice with the diameter of about 60 nn and the length of 4-5 pm respectively, and grew along [001] axis. It was found that the concentration of FeC13 solution could extremely affect the growth ofp-Fe00H nanowires and only under appropriate concentration high quality nanowires could be obtained. Keywordsp-Fe00H; nanowire; hydrolysis 近年来，一维纳米材料(纳米管、纳米棒、纳米带等) 以其特殊的物性及在纳米器件方面的潜在应用，受到了 广泛关注.一维纳米材料尺寸小、比表面积大，从而使 它的磁性质、电性质、催化性质等物理化学性质与其体 相材料不同[[l].目前，一维纳米材料的制备方法有许多 种，如模板法[2,31、 VLS法[[4,51、SLS法16,71. CVD法[81 反胶束法[91和溶剂热法等1101.利用这些方法人们获得了 各种各样的一维纳米材料.从应用的角度，探索制备条 件更为温和、方法更为简单，适宜大量生产的具有良好 晶型的纳米线制备技术是人们首先追求的目标. [3-Fe00H作为y-FeA磁粉的前驱体，它的形态和 结构决定着y-Fe203磁粉的应用范围.例如，针形或纺 锤形y-Fe203由于轴比较大，可满足垂直磁记录介质需 要高矫顽力的要求.据测定，针形y-Fe203矫顽力的 67%来源于形状各向异性，磁晶各向异性仅占33%]. 因此，控制P-Fe00H的轴比是调控y-Fe203磁性质的一 个重要因素.而p-Fe00H纳米线具有更大的轴比，相信 在垂直磁记录介质中会有更广泛的应用前景.另外， p-Fe00H是一种优良的半导体材料，带隙为2.12 eV,可 用于氧化一还原反应，也可用于煤加氢反应的催化剂. *E-mail: zld@henu.edu.cn Received June 7, 2004; revised