外墙渗漏水的力学分析.pdfVIP

外墙渗漏水的力学分析 胡 骏※1 摘要 造成建筑外墙渗漏水的因素很多，而针对外墙渗漏水的有效防水措施却很少，这与我们对造成外墙渗漏 水原因和机理的研究还不够深入有关。本文运用材料力学、结构力学、气象学等方法，分析了降雨、风压对外墙 渗漏水的影响；材料硬化收缩、气温变化对墙面裂缝开展的影响；强风时窗户的变形，在墙体交接部位出现裂缝 等问题，同时就这些问题提出了初步建议。防水工程学有很多问题可以采用力学方法进行定量的分析，虽然不一 定与实际情况完全相符，但可以得出定性分析结论，以正确引导工程应用，为建筑外墙防水设计提供了理论依据。 Mechanical Analysis of Water Leakage through Exterior Wall Hu Jun ABSTRACT ：Water leakage through the exterior wall of building is the unexpected results derived from many factors. However, there is few effective measure to change such negative circumstance because of the few knowledge on the sound reasons and mechanism related to leakage till now. In the paper, by applying material mechanics, structure mechanics and meteorological principles and methods, the effects of rain-fall and wind pressure load on the exterior wall, shrinkage related to the cementitious material curing and temperature-dominated expansion of cracks on the exterior wall as well as the junctures width variation around the window frame upon the heavy wind-load were analyzed 1. 前 言 地区雨水充沛，夏季常受台风影响，经常有暴雨 造成外墙渗漏水的原因很多，不同的外墙形 和大暴雨天气。年降雨量通常在 1500mm 以上， 式、结构形式、饰面材料、墙体构造、门窗构件 许多城市年降雨量在2000mm 以上，基本风压高 布置，都会影响到外墙防水性能。其中，降雨量 达 0.5～1.0kN/㎡。邻国日本与韩国的平均年降 和气候环境是主要的外界因素，结构形式设计， 水量均在1500mm左右，部分地区超过2000mm， 各种材料的选用和质量是内在因素，施工质量控 与中国相比，日本和韩国的各地年降水量比较均 制是管理因素。无论何种因素，最后会集中到墙 衡。 面受雨水的影响程度及墙面抗渗漏的能力二个 雨滴在下落过程中，大小与速度是不断变化 要素上。本文将针对这两个要素，从力学角度分 的。降雨强度越大，相应雨滴直径越大，雨速也 析降雨、风压、温差变形、材料收缩变形、门窗 越快。雨滴在下降过程中会破裂成大小不等的雨 构件风压变形等因素的影响，找出造成墙面渗漏 粒，大暴雨雨滴最大直径约有 5~6mm，表 1 中 水的主要影响因素。 所列直径是指D50 （占50% 比例）的平均直径。 雨滴在重力与空气阻力的共同作用下，其收尾速 2. 雨强、雨速、雨滴大小 度通常近乎是匀速的，暴雨雨滴的终点速度在 在进行渗漏分析前，我们先把引起渗漏的 7m/s 左右，见 （表 1）