原材料对高性能混凝土强度的影响.pdfVIP

原材料对高性能混凝土强度的影响 周炳常 摘要：随着现代化混凝土技术的发展， 具良好的施工性能，高体积稳定性，满 足实际抗压强度的要求，以及优异耐性的高性能混凝土逐渐成为工程界研究和应 用的热点。混凝土结构物主要都是用于承受荷载或抵抗各种作用力，而混凝土是 按强度进行设计，强度是混凝土最重要的力学性能，是对混凝土质量的最终标准。 在高性能混凝土中，影响其强度的涉及原材料、水胶比、砂率、养护等一系列诸 多因素。而原材料的选用对混凝土的强度更是有着十分重要的影响。 关键词：高性能混凝土；强度；原材料 Abstract: with the development of modern concretetechnology, good construction performance,high volume stability, satisfy the requirements of the compressivestrength, and excellent patience ofthe high performanceconcrete gradually become the hot spot of the engineering researchand application. Concrete structures weremainly used to bearloads or against a variety of force, and concrete isthe strength to carry on the design, strength isthe most important mechanics performance of concrete,isthe finalon concrete quality standard. In high performanceconcrete, affect their strength of the concernsof raw materials, water-binderratio, sand ratio, maintenance and soon aseriesof many factors.And the selection ofraw materials to the concrete strength but alsohas avery important impact. Keywords: high performance concrete; Strength; Raw materials 中图分类号：TU37 文献标识码：A 文章编号： 高性能混凝土具有丰富的技术内容，尽管业界对高性能混凝土有不同的定义 和解释，但彼此均认为高性能混凝土的基本特征是按耐久性进行设计，保证拌和 物易于浇筑和密实成型，不发生或尽量少发生因温度和收缩产生的裂缝。硬化后 有足够的强度，内部空隙结构合理而有低渗透性和高抗化学侵蚀性。其中强度尤 为重要。工程上对混凝土的其他性能要求，如耐久性、不透水性、抗侵蚀性等， 这些性能都与混凝土的强度有着密切关系。因为一般来说，混凝土的强度越高， 其密度也越高，其刚性、耐久性、不透水性、抗侵蚀性等也将提高。而随着工程 建设的需要，高性能混凝土的使用频率越来越高。尤其近年来预应力混凝土的应 用范围逐渐推广到更多的结构领域，如大跨超长、超厚及超静定框架结构，其混 凝土强度等级必须提高。而且泵送施工，更是必不可少的环节。因此，对其进行 严格质量控制的重要性也越来越强。 1 1 11 水泥 水泥是混凝土工程的主要材料，水泥的品质直接影响混凝土的质量。当水灰 比相等时，高标号水泥比低标号水泥配制出的混凝土抗压强度要高许多。随着水 泥细度增加，水化速率增大，会导致较高的强度增长率。但应该避免细磨粉的含 量。因为当颗粒很细时，粒径在1um以下的颗粒不到一天就完全水化，几乎对后 期强度没有任何贡献。而另外直径大于60um的颗粒对强度也并不起作用。在水 泥品种及混合材料掺量相同的情况下，水泥粉磨细度细，比表面积大，其制备的 混凝土需水性无疑会高。若要保证混凝土具有良好的流动性，就会增加水或水泥 还有减水剂，从而对混凝土的强度也带来影响。除此之外，水泥颗粒的级配的影 响也有一定作用。良好的颗粒级配可以降低混凝土的孔隙率，从微观角度上说对 强度也会发生影响。由此可见，水泥的细度对混凝土强度是有一定的影响。水泥 强度主要来自于早期强度C