不锈钢化学成分、特性、用途.docVIP

不锈钢化学成分和统一数字代号 序号 统一数 字代号 牌号 化 学 成 分，% C碳 Si硅 Mn锰 P磷 S硫 Ni镍 Cr铬 Mo钼 其他 1 S30210 1Cr18Ni9 ≤0.15 ≤1.00 ≤2.00 ≤0.035 ≤0.030 8.00~10.00 17.00~19.00 / / 2 S30408 0Cr18Ni9(304) ≤0.07 ≤1.00 ≤2.00 ≤0.035 ≤0.030 8.00~11.00 17.00~19.00 / / 3 S30403 00Cr19Ni10(304L) ≤0.03 ≤1.00 ≤2.00 ≤0.035 ≤0.030 8.00~12.00 18.00~20.00 / / 4 S31800 0Cr25Ni20(310S) ≤0.08 ≤1.00 ≤2.00 ≤0.035 ≤0.030 19.00~22.00 24.00~26.00 / / 5 S31600 0Cr17Ni12Mo2(316) ≤0.08 ≤1.00 ≤2.00 ≤0.035 ≤0.030 10.00~14.00 16.00~18.00 2.00~3.00 / 6 S31603 00Cr17Ni14Mo2(L) ≤0.03 ≤1.00 ≤2.00 ≤0.035 ≤0.030 12.00-15.00 16.00-18.00 2.00~3.00 / 7 S32168 0Cr18Ni10Ti(321) ≤0.08 ≤1.00 ≤2.00 ≤0.035 ≤0.030 9.00-12.00 17.00-19.00 / Ti≥5×C% 8 S30210 1Cr18Ni9Ti ≤0.12 ≤1.00 ≤2.00 ≤0.035 ≤0.030 8.00-11.00 17.00-19.00 / Ti≥5×C%-0.02) ~0.80 9 S34778 0Cr18Ni11Nb ≤0.08 ≤1.00 ≤2.00 ≤0.035 ≤0.030 9.00-13.00 17.00-19.00 / / 10 S11510 1Cr15 ≤0.12 ≤1.00 ≤1.00 ≤0.035 ≤0.030 / 14.00-16.00 / / 11 S11710 1Cr17 ≤0.12 ≤0.75 ≤1.00 ≤0.035 ≤0.030 / 16.00-18.00 / 允许含有≤0.6%Ni 12 S41008 0Cr13 ≤0.08 ≤1.00 ≤1.00 ≤0.035 ≤0.030 / 11.50-13.50 / 允许含有≤0.6%Ni 13 S41010 1Cr13 ≤0.15 ≤1.00 ≤1.00 ≤0.035 ≤0.030 / 11.50-13.50 / 允许含有≤0.6%Ni 14 S11603 00Cr12Ti ≤0.025 ≤0.80 ≤0.80 ≤0.035 ≤0.020 / 10.5-12.5 / Ti 6×C%~0.75 注：1Cr18Ni9Ti不推荐使用 钢号 不锈钢管特性 用途 奥 氏 体 钢 301 17Cr-7Ni- 低碳 与 304 钢相比， Cr 、 Ni 含量少，冷加工时抗拉强度和硬度增高，无磁性，但冷加工后有磁性。 列车、航空器、传送带、车辆、螺栓、螺母、弹簧、筛网 301L 17Cr-7Ni-0.1N- 低碳 是在 301 钢基础上，降低 C 含量，改善焊口的抗晶界腐蚀性；通过添加 N 元素来弥补含 C 量降低引起的强度不足，保证钢的强度。 铁道车辆构架及外部装饰材料 304 18Cr-8Ni 作为一种用途广泛的钢，具有良好的耐蚀性、耐热性，低温强度和机械特性；冲压、弯曲等热加工性好，无热处理硬化现象（无磁性，使用温度 -196 ~800 ℃）。 家庭用品（ 1 、 2 类餐具、橱柜、室内管线、热水器、锅炉、浴缸），汽车配件（风挡雨刷、消声器、模制品），医疗器具，建材，化学，食品工业，农业，船舶部件 304L 18Cr-8Ni- 低碳 作为低 C 的 304 钢，在一般状态下，其耐蚀性与 304 刚相似，但在焊接后或者消除应力后，其抗晶界腐蚀能力优秀；在未进行热处理的情况下，亦能保持良好的耐蚀性，使用温度 -196 ~800 ℃。 应用于抗晶界腐蚀性要求高的化学、煤炭、石油产业的野外露天机器，建材耐热零件及热处理有困难的零件 304Cu 13Cr-7.7Ni-2Cu 因添加 Cu 其成型性，特别是拔丝性和抗时效裂纹性好，故可进行复杂形状的产品成形；其耐腐蚀性与 304 相同。 保温瓶、厨房洗涤槽、锅、壶、保温饭盒、门把手、纺织加工机器。 304N1 18Cr-8Ni-N 在 304 钢的基础上，减少