单分散聚苯乙烯胶体颗粒的界面电性质研究.pdfVIP

《化学通报》在线预览版 单分散聚苯乙烯胶体颗粒的界面电性质研究 * 刘丽 严亚 陈启明 (华东师范大学胶体与界面化学研究所,上海,200062) 摘 要 以过硫酸钾(KPS)为引发剂，以水为反应介质，采用无皂乳液聚合工艺，制备出粒径在 500nm 左右单分散(分散 系数5%)聚苯乙烯微球。所制备的聚苯乙烯微球为光滑的球形颗粒。研究发现；由无皂乳液聚合法制备的胶体颗粒其 ζ 电势在不同的离子强度下随pH 的变化曲线均出现平台pH6～10.5，说明在一定的离子强度和pH 条件下，聚苯乙烯胶乳 的 ζ电势具有良好的稳定性。聚苯乙烯胶乳有望作为具有一定电势值的标准颗粒。 关键词 聚苯乙烯 无皂乳液聚合 界面电性质 ζ电势 The Study of Monodisperse Polystyrene Microsphere’s interface electrical properties * Liu Li, Yan Ya, Chen Qimin (Chemistry department of east China normal university, shanghai 200062) Abstract The water systems have been exploited as dispersion medium in soap-free polymerizing of polystyrene (PS) using potassium persulfate as an initiator.The size of particles is round 500nm(coefficient of variation 5 %). The study on the curves of Zeta-potential (ζ) versus pH in different ionic strength showed that the polystyrene colloidal particles prepared by soap-free emulsion polymerization are rather stable their ζ-potential were invariable with the pH varied from 6 to 10.5, so the PS microspheres could be as a model particlesfor its ζ-potential value. Key words Polystyrene Soap-free emulsion polymerization, Interface electricity property, ζ- potential 微米级颗粒度均匀的聚合物微球，作为功能高分子材料，在分析化学、生物化学、免疫医学、标准计量、 色谱分离以及某些高新技术领域中有着广泛的用途, 因而对这类材料的研究越来越引起了重视[1~5] 。聚 合物微球的稳定性也受到了越来越多的关注。本文采用无皂乳液聚合法制备出单分散的聚苯乙烯胶乳。 该法的聚合工艺已经有很多报道，但是对于其胶体稳定性特别是界面电性质的研究国内文献还鲜有报 道。 ζ电势是衡量胶体颗粒稳定性的一个重要指标，ζ电势不是恒定的，它的数值决定于滑移面位置， 而滑移面的位置与测定条件、方法有关。如果固相所固定的液层较厚，或扩散层的厚度较小，则 ζ电势 就较低，如果固相所固定的液层较薄，或扩散层厚度较大，则 ζ电势就较高。因此ζ电势不仅取决于胶 体粒子的性质而且与实验条件有关。通过改变离子强度、pH 、某些离子的浓度等，使得 ζ电势趋向于零， 此决定电势为零的条件称为等电点(Isoelectric Point)。通过对不同样品在不同离子强度下 ζ电势随pH 的 变化曲线的研究发现，所制备的聚苯乙烯均匀胶乳存在等电点，且等电点在强酸