《Enhanced Electric Double LayerCapacitance of Graphite Oxide》.pdfVIP

E L Enhanced Electric Double Layer C Capacitance of Graphite Oxide I Intercalated by Poly(sodium 4- T styrensulfonate) with High Cycle Stability R Hae-Kyung Jeong,† Meihua Jin,† Eun Ju Ra,† Kyeu Yoon Sheem,‡ Gang Hee Han,† Sivaram Arepalli,† and Young Hee Lee†,* †BK21 Physics Division, Department of Energy Science, Center for Nanotubes and Nanostructured Composites, Sungkyunkwan Advanced Institute of Nanotechnology, A Sungkyunkwan University, Suwon 440-746, South Korea, and ‡Energy Lab., Corporate RD Center, Samsung SDI, Yongin 446-577, South Korea mal annealing at 100 °C required in the ABSTRACT We propose a new material for high power and high density supercapacitors with excellent cycle manufacture of supercapacitor elec- stability. Graphite oxide (PSS GO) intercalated with poly(sodium 4-styrensulfonate) showed high performance trodes.11 Introduction of a simple thermally of electric double layer capacitance (EDLC) compared to that of the pristine graphite oxide. Specific capacitance of stable bridge between the interlayers of graphite oxide will make the interior layers the PSS GO reached 190 F/g, and the energy density was much improved to 38 Wh/kg with a power density of available for ion storage/retrieval. This pa- 61 W/kg. Cycle test showed that the specific capacitance decreased by only 12% after 14860 cycles, providing per reports the enhanced performance of a excellent cyclic stability. The hig