2007 中国钢铁年会论文集 钢包底吹氩工艺技术改进 米 源 李凤喜 邹继新 韩树良 （武汉钢铁（集团）公司第三炼钢厂, 武汉 430083 ） 摘 要 分析了影响钢包底吹氩成功率的各种因素，包括透气砖的抗钢水渗透性能、抗熔渣渗透性能、透气 砖抗热震性、钢包透气砖的清理维护、底吹管道、转炉出钢操作、氩气源压力以及大钢包温降大等因素， 提出了相应改进措施。实施相应的措施后，通过实践使钢包底吹氩成功率由 90％提高到 99％，满足了品种 钢的生产需要。 关键词 钢包 透气砖 底吹氩 Technology and Improvement of Argon Blowing from Bottom of Ladle Mi Yuan Li Fengxi Zou Jixin Han Shuliang （No.3 Steelmaking Plant of WISCO,Wuhan, 430083 ） Abstract Factors influencing the hit rate of ladle bottom argon bubbling are analyzed, including the anti-molten steel permeate function of the permeable brick, the anti-flag permeate function of the permeable brick, hot earthquake of the permeable brick, the tidying up and maintenance of the brick, the piping of the bottom blow, tapping operation ,argon source pressure and the temperature drop of ladle. And improvement measure is put forth. The hit rate of ladle bottom argon bubbling has increased from 90 ％ to 99 ％ by practice .The demand of grade steels are well satisfied. Key words ladle, permeable brick, bottom argon bubbling 钢包底吹氩工艺是炼钢过程中一个十分重要的环节 ，它的作用是对钢水进行搅拌。钢包底吹氩气吹入钢 水中，以气泡形式分散于钢水并上浮，周围的钢水受浮力的驱动，在透气砖上方形成向上流股，达到钢液顶 部向水平方向转向，然后沿钢包壁处向下返流，使钢水在钢包内循环流动，从而使添加在钢水中的合金、熔 剂等快速熔化，促进了钢液成分和温度的均匀以及钢液中夹杂物的上浮，去除了钢中的非金属夹杂物和有害 气体，达到精炼钢液的目的。 武钢某炼钢厂钢包在2006 年的一段时期里频繁发生钢包底吹不透气现象，钢包底吹成功率仅为90 ％。 随着品种钢比例的不断提高，钢包底吹氩成功率低，不能满足生产的需求。为了提高钢包底吹成功率，针对 钢包底吹氩失败的原因进行了分析，同时提出了相应的对策。 1 钢包底吹氩存在的问题及影响因素 1.1 钢水渗入吹气通道堵塞透气砖 透气砖使用条件较为苛刻，300t 钢包钢水深约 4 m ，静压力大，同时钢水搅拌强度大，需要透气砖抗钢 水渗透能力强。在实际生产中，经常发生透气砖表面结冷钢渣难以清理干净，容易发生底吹失败现象。这是 由于钢水在静压力的作用下进入砖缝内，随温度的降低而逐渐凝固，堵塞透气砖吹气通道，从而引起底吹弱 甚至吹不通。冷钢堵塞透气砖吹氩缝照片见图 1。 要使钢水不渗入透气砖狭缝，就须使钢水的静压力P 静与透气砖狭缝对钢水的附加压力P 附 （即毛细管 张力）处于平衡状态。钢水渗入