Nd3掺杂对尖晶石型镍铁氧体吸波性能的影响郭磊.pdfVIP

Nd3+ 102205 -Nd3+ NiNd Fe O X x 2-x 4 1000 Nd3+ x=0.04 Nd3+ Nd3+ Nd3+ x=0.02 47dB10dB 4.5GHz Nd3+ TM25; TM277+.1 A 1001-3830(2013)05-0019-04 Influence of Nd3+ dopant on the microwave absorbing properties of nickel spinel ferrite GUO Lei, YU Jian-hua, LI Zhi-jun, WANG Pu-hong, DING Zhi-jun, DU Bin Research Institute of Chemical Defense, Beijing 102205, China Abstract: Nd3+-doped nickel spinel ferrite were prepared by sol-gel method. The microstructural and electromagnetic properties were analyzed by TG-DSC, X-ray diffraction and vector network analyzer. Impedance matching solution maps is used to obtain the matching frequency and thickness. Based on the matching frequency and thickness, microwave absorption of the material was studied. The result shows that the annealing temperature should be higher than 1000 and Nd3+-dopedt nickel spinel ferrite is prepared when the doping amount of Nd3+ is reduced to 0.04. It is found that the amount of Nd3+ dopant could affect the electromagnetic parameters and microwave absorbing properties of nickel ferrite. With decreasing doping amount, the matching thickness and minimum reflectance peak decrease gradually and the absorption peak shifts to higher frequency. When the amount of Nd3+ dopant is 0.02, the minimum reflectance is 47dB, and effective 10dB bandwidth reaches 4.5GHz . Key words: nickel ferrite; Nd3+ dopant; electromagnetic parameters; matching thickness; microwave absorbing properties  [3-7] 1