硅钼酸钾盐TiO2的合成及其光催化性能研究.doc

齐 齐 哈 尔 大 学 毕业设计（论文） 题目/TiO2的合成及光催化性能研究 学院 专业班级 学生姓名 指导教师 成绩 2011 年月日 摘 要 本文采用浸渍法制备TiO2负载光催化剂。用红外光谱、X-射线粉末衍射进行表征，结果表明：合成的催化剂仍具有Keggin结构N2吸附-脱附考察了催化剂的比表面结、孔径，表明产物为介孔材料。在紫外光照射下，研究影响催化剂降解的因素，分别考察了催化剂的用量、甲基橙的初始浓度、溶液的pH值、30%H2O2的用量、脱色时间等因素对脱色率的影响，最佳条件为：催化剂加入量为80 mg·L-1、pH=1.01、30%的H2O2用量10mL·L-1 ，脱色率达以上关键词：杂多酸； K8SiMo11/TiO2 photocatalyst was prepared by impregnation. IR, X-ray powder were used to character the production and the synthetic catalyst still has Keggin structure. With TGA thermal stability of the catalyst, the results showed that：the catalyst was stable. By N2 adsorption-desorption of catalyst surface area results, the pore size,mesoporous materials that the product is.Under UV irradiation, study the factors that affect the degradation of the catalyst, the amount of catalyst, respectively, pH of the solution, 30% H2O2 in the amount of bleaching time on the decolorization rate of the best conditions：Methyl orange degradation percentage of over 93％ was obtmned under the following conditioninitial concentration of methyl orange =10 mg·L-1, catalyst dosage 80 mg·L-1, H2O2(30％) of 10 mL·L-1pH=1.01, reaction for 180 min. Key words：eteropoly acid；Titanium dioxide；atalyst；Methyl orange摘 要 I Abstract II 第1章 绪 论 1 1.1 杂多化合物的概述 1 1.1.1 杂多酸化合物的基本特征 1 1.1.2 杂多酸具备优异的催化性质 2 1.1.3 杂多酸（盐）催化剂在光降解中的应用 2 1.2 二氧化钛的性质和用途 3 1.3 负载杂多酸盐的概述 3 1.3.1 负载杂多酸盐的合成方法 3 1.3.2 负载杂多酸盐光催化的应用及前景 4 第2章 实验部分 5 2.1 实验仪器与试剂 5 2.1.1 实验仪器 5 2.1.2 实验试剂 5 2.2 合成方法 6 2.2.1 缺位Keggin结构硅钼酸钾盐(K8SiMo11·nH2O)的合成 6 2.2.2 硅钼酸钾盐/ TiO2的合成 6 2.3 表征方法 6 2.3.1 红外光谱表征 6 2.3.2 X-射线固体粉末衍射(XRD) 6 2.3.3 N2吸附-脱附表征 6 2.3.4 热性质分析 6 2.4 硅钼酸钾盐/TiO2光催化性能的研究 7 第3章 结果和讨论 8 3.1 催化剂的表征 8 3.1.1 红外光谱表征 8 3.1.2 X-射线固体粉末衍射(XRD)表征 9 3.1.3 氮气脱附-脱附吸附吸附光谱表征 10 3.1.4 热稳定分析 11 3.2 硅钼酸钾盐/TiO2光催化降解甲基橙实验 12 3.2.1 硅钼酸钾盐/TiO2合成的正交实验 12 3.2.2 对照实验 13 3.2.3 催化剂的加入量 16 3.2.4 甲基橙初始浓度 16 3.2.5 过氧化氢用量对甲基橙降脱色率的影响 17 3.2.6 甲基橙初始酸度对脱色率的影响 18 3.3 最优条件下催化剂、硅钼酸钾盐和TiO2降解甲基橙 18 结 论 1