低合金高强度钢动态断裂行为的研究.pdfVIP

钢铁/981013 钢 铁 科技期刊 IRONSTEEL 1998年１０月第33卷第10期 低合金高强度钢动态断裂行为的研究 李存剑　李少华　　翁宇庆　　秦瑞凯　　 　(钢铁研究总院)　(国家冶金工业局)(鞍山钢铁(集团)公司) 摘　要　低合金高强度钢的动态断裂韧性在一定条件下受控于温度和加载速率的变化，降低温度 和提高加载速率都会使钢的动态断裂韧性降低。通过热激活分析，可以获得定量描述动态断裂韧 性、温度及加载速率之间的关系。 关键词　高强度钢　动态断裂韧性　热激活分析 DYNAMIC FRACTURE BEHAVIOR OF LOW ALLOY HIGH STRENGTH STEEL LI Cunjian　LI Shaohua (Central Iron and Steel Research Institute) WENG Yuqing (State Administration of Metallurgical Industry) QIN Ruikai (Anshan Iron and Steel (Group) Co.) ABSTRACT　The dynamic fracture toughness of low alloy high strength steel is dependent on the temperature and loading rate in some range.With decreasing temperature or increasing loading rate the dynamic fracture toughness will be decreased.A quantitative relationship between dynamic fracture toughness and temperature and loading rate has been obtained through thermal activation analysis. KEY WORDS　highstrength steel,dynamic fracture toughness,thermal activation analysis 　　研究温度和加载速率对高强度钢变形及断裂行为的影响对保证其结构件的安全使用有着重要 的实际意义。目前钢的动态屈服强度随温度和速率的变化规律已得到广泛的研究，并且其变形过 ［1，2］ 程受热激活控制已得到证实 。但是对钢的动态断裂韧性的研究大多数是在一定的加载条 ［3］ 件下，研究温度对其的影响 ，而系统地研究温度和速率两种因素同时变化的情况则较少，尤 其缺乏两种因素对试验结果影响的定量理论分析研究。 1　试验材料及方法 1)。三点弯曲试样尺寸为130 mm×14 mm×28 mm，按标准GB4161—84制样，线切割缺口方向T- L，预疲劳裂纹频率为92 Hz。用无水乙醇和液氮来调节试验所需温度。 　　试验在MTS—880型动静态材料试验机上进行，当加载位移速率 ＝0.01和0.7 mm/s时，用X- Y记录仪记录P-Δ曲线；对于＝50 mm/s的快速三点弯曲试验，用计算机数据采集处理系统记录P- Δ曲线。 万方数据 file:///E|/qk/gt/981013.htm（第 1／6 页）2010-3-22 20:32:33 钢铁/981013 图 1　试验用钢的显微组