《挤压态喷射沉积7075AlSiC颗粒增强复合材料热压缩流变应力行为及加工图（英文版）》.pdfVIP

Trans. Nonferrous Met. Soc. China 25(2015) 692−698 Flow stress behavior and processing map of extruded 7075Al/SiC particle reinforced composite prepared by spray deposition during hot compression 1 1,2 1 1,2 Hong-dan WU , Hui ZHANG , Shuang CHEN , Ding-fa FU 1. College of Materials Science and Engineering, Hunan University, Changsha 410082, China; 2. Key Laboratory for Spray Deposition Technology and Application of Hunan Province, Hunan University, Changsha 410082, China Received 29 April 2014; accepted 7 November 2014 Abstract: Hot compression tests of the extruded 7075Al/15%SiC (volume fraction) particle reinforced composite prepared by spray −1 deposition were performed on Gleeble−1500 system in the temperature range of 300−450 °C and strain rate range of 0.001−1 s . The results indicate that the true stress−true strain curve almost exhibits rapid flow softening phenomenon without an obvious work hardening, and the stress decreases with increasing temperature and decreasing strain rate. Moreover, the stress levels are higher at temperature below 400 °C but lower at 450 °C compared with the spray deposited 7075Al alloy. Superplastic deformation characteristics are found at temperature of 450 °C and strain rate range of 0.001−0.1 s−1 with corresponding strain rate sensitivity of 0.72. The optimum parameters of hot working are determined to be temperature of 430−450 °C and strain rate of 0.001−0.05 s−1 based on processing ma