毕业设计（论文）_蒙脱石混悬液的制备工艺研究.docVIP

提供全套毕业论文图纸，欢迎咨询 山西医科大学本科生毕业论文 论文题目 学生姓名 学 号 200864 指导老师 专 业 班 级 2010年6月 学生姓名： 指导老师：【摘要】目的:。方法:,本文采取单因素考察方法考察了制备工艺、助悬剂、蒙脱石与助悬剂用量比等因素，确定了蒙脱石混悬液的最佳制备工艺，考察了制剂的稳定性并对其做了质量标准研究。结果:结论:【关键词】；； The research of the technology of the preparation of montmorillonite suspension 【Abstract】 Objective: To the technology of preparation of montmorillonite suspension and preparation quality standard. Methods: During the research of preparation of montmorillonite suspension, the effect of factor including the technology of preparation, the suspension aid and the ratio of amount of montmorillonite to that of suspension aid on the stability of preparation suspensions were investigated by single-study. Formulation was optimized finally. Meanwhile we have detected preparation quality standard. Results: The formulation is: the second technology of preparation and the 0.2% of amount of montmorillonite to that of Sodium Tylose. Conclusion: The stability of preparation suspension is better. The effects are satisfactory. 【Key Words】 ; suspension; the technology of preparation; suspension aid; preparation quality standard 蒙脱石混悬液的制备工艺研究 前言 ）。2．材料与仪器 2.1 材料 （，有限公司），甲基纤维素（，），（，厂），（），，磷酸二氢钠，氢氧化钠均为分析纯。 2.2 仪器 （，科技开发公司），UV75B紫外分光光度计（上海精密科学仪器有限公司），（），3．实验方法3.1 蒙脱石混悬液制备工艺的选择 3.1.1 混悬液的制备方法的选择 混悬液的制备原则首先是使粉粒润湿并在液体分散介质中均匀分散，保持一定条件使其尽量不聚集，然后采取一定的措施防止结块。 制备方法通常混悬液的有两种：分散法和凝聚法。由于蒙脱石本身的性质我们采用的是分散法，以制备10ml含1g蒙脱石，3%PVP助悬剂为例，其工艺途径可阐述如下： 工艺一：称取1.0g蒙脱石于带塞的试管中，另取约0.3gPVP，使溶于10ml的蒸馏水中，待PVP溶液透明混匀后到入装有蒙脱石的试管中，密盖后，在液体快速混合器中以5000r∕min，涡旋振摇30min，即得。 工艺二:称取1.0g蒙脱石和0.3gPVP，置试管中，充分混匀后，取10ml蒸馏慢慢边滴加蒸馏水边用玻璃棒搅拌，在蒙脱石全部湿润后，混合液呈浆糊状态时，把剩余的蒸馏水全部加入试管中，密盖后，在液体快速混合器中以5000r∕min ，涡旋振摇30，即得。 3.1.2 评定混悬液质量方法的选择。3.1.2.2 沉降体积比的测定 沉降体积比（sedimentation rate）。3.1.2.3重新分散试验 优良的混悬液经过贮存后再振摇，沉降物应能很快重新分散，这样才能保证服用时的均匀性和分剂量的准确性。试验方法：将混悬液置于100ml量筒内，以每分钟20转的速度转动，经过一定时间的旋转，量筒底部的沉降物应重新均匀分散，说明混悬液再分散性良好。 我们以用量为0.4%的羧甲基纤维素钠为助悬剂以沉降体积比为评定标