产万吨聚苯乙烯工艺设计教程.docVIP

毕 业 设 计 题 目： 年产8万吨聚苯乙烯工艺设计 学 院： 化学与材料工程学院 专 业： 高分子材料与工程 姓 名： 苏隆辉 学 号： 102410236 指导老师： 王宁 完成时间： 设计说明 可发性聚苯乙烯（Expandable EPS）通称聚苯乙烯和苯乙烯系共聚物，是一种树脂与物理性发泡剂和其它添加剂的混合物。可发性PS可被加工成低密度（0．7—10．0ib／ft3）的泡沫塑料剂品。最常见的可发性聚苯乙烯是含有作为发泡剂的戊烷的透明PS粒料。Expandable Polystyrene (Expandable Polystyrene, referred to as EPS) commonly known as the Department of polystyrene and styrene copolymer is a resin with the physical blowing agent and other additives mixture. EPS can be processed into low-density (0.7-10.0ib/ft3) goods of the foam agent. The most common is to be made of polystyrene with n-pentane as a blowing agent aggregates of transparent PS. The design for the annual production capacity of 80，000 tons can be made of polystyrene polymerization process design section, the reaction mechanism is free radical polymerization, suspension polymerization process used to styrene as monomer, water suspension medium done using one-step production of low-temperature suspension polymerization process. This method is a styrene monomer, initiator, dispersing agent, water, blowing agent and other auxiliaries to join reactor, the polymer containing a foaming agent, after the resin particles by washing, centrifugal separation and drying, the system may be made of polystyrene beads products; in this section based on the polymer material balance, heat balance, equipment selection, the mapping of control points with the flow chart, diagram and layout of piping plans and the preparation of the design specification and calculation of the book. Key Words：Expandable polystyrene，Suspension Technique，Craft calculation，Technological design. 1 总论 1.1概论 聚苯乙烯是指由苯乙烯单体经自由基缩聚反应合成的聚合物，英文名称为Polystyrene, 简称PS。它是一种无色透明的热塑性塑料，具有高于摄氏100度的玻璃转化温度，因此经常被用来制作各种需要承受开水的温度的一次性容器，以及一次性泡沫饭盒等。通常的聚苯乙烯为非晶态无规聚合物，具有优良的绝热、绝缘和透明性，长期使用温度0～70，但脆，低温易开裂。此外还有全同和间同立构聚苯乙烯。全同聚合物有高度结晶性。聚苯乙烯（PS