毕业论文9-杨延丽_new概述.doc

毕 业 论 文 题 目： 粉煤灰制备透水砖工艺优化 学 院： 土木工程学院 专 业： 无机非金属材料工程 姓 名： 杨延丽 学 号： 013410209 指导老师： 王继娜 完成时间： 2014年5月25号 助熔剂%，温度1050℃，保温时间min；（2）粉煤灰掺量45%，助熔剂%，温度1℃，保温时间min。 关键字：粉煤灰，透水砖，正交实验，抗压强度，透水系数 Abstract The Permeable brick,a new kind of building material with wonderful water permeability and water-retention,can well retard urban desert and heat island effect which come from the road surfacing of bound waterproof pavement. the thesis uses fay ash，which comes form Pingdingshan,as main raw material, the influence,which is caused by the dosage of fly ash,dosage of flux ,calcination temperature and soaking time,of the property of permeable brick by means of orthogonal experiment method ,in order to research the feasibility of making permeable brick with fly ash. the results show that the influence of various factors ,implying on the compressive strength is different,top to bottom are the dosage of fly ash calcination temperature,soaking time and the dosage of flux. two groups more reasonable technological parameters for this study are followed:(1)45% dosage of fly ash,4% dosage of flux,calcination temperature 1050℃,soaking time 60min.(2)45% dosage of fly ash,5% dosage of flux,calcination temperature1100℃,soaking time 60min. Key words:fly-ash, permeable brick, orthogonal, compressive strength, permeability coefficient 目录 摘要 I Abstract II 目录 Ⅲ 1绪论 1 1.1课题的研究背景及意义 1 1.1.1课题的研究来源 1 1.1.2课题的研究目的与意义 1 1.2国内外研究现状 2 1.2.1国内研究现状 2 1.2.2国外研究现状 3 1.3研究内容 4 2实验材料与实验方法 5 2.1实验材料 5 2.2实验仪器 5 2.3实验方法 6 2.3.1实验方法的选择 6 2.3.2工艺流程 6 2.3.3实验方案 6 2.3.4试件的制备 7 3实验结果与分析 8 3.1实验结果 8 3.1.1 结果分析 8 4结论 13 5参考文献 21 6致谢 21 11.1课题的研究背景及意义 近来国内建筑行业的快速发展，混凝土、水泥等建筑材料一路增长。根据调查，11年国内的水泥产量为20.85亿吨，在整个世界水泥行业内位列前茅。但是在水泥发展迅猛的同时造成了能源浪费和环境的严重污染。经长期调查研究，每生产1吨水泥需要1.7吨生料，其中包括耗约标准煤120千克，而污染更严重向大气排放约0.