表面与界面XPS摘要.ppt

* XPS应用－催化研究 Fig3. The XPS spectra of film catalyst poisoned at 500℃ for 1 h (A) Co 2p (B) S 2p * XPS应用－薄膜材料研究 Figure 1 The Ti 2p spectra of PZT layer in PZT/Si and PZT/Pt(140 nm)/Si film sample Figure 2 The C 1s spectra of PZT layer in PZT/Si and PZT/Pt(140 nm)/Si film sample * XPS应用－薄膜材料研究 Figure 2 The Si 2p spectra of PZT layer in PZT/Si and PZT/Pt(140 nm)/Si film sample * XPS应用－材料合成 * 材料的表面改性 * 材料的表面改性 * XPS的新进展 单色化XPS 小面积XPS 成像XPS * 图像XPS分析 SPS Photo of Paint System Cross-section Polyethylene Substrate Adhesion Layer Base Coat Clear Coat Mapping Area 695 x 320μm 1072 x 812mm * C O 695