聚氨酯涂料毕业论文总结.docVIP

本科毕业设计(论文)题目： 院 （系）： 专 业： 班 级： 学 生： 学 号： 指导教师： 2013年 06月环氧树脂改性聚氨酯防腐涂料的制备与性能研究 摘要 Abstract In this experiment, toluene diisocyanate(TDI) and polyethylene glycol(PEG) asraw material composes polyurethane prepolymer, and then adds simethiconeepoxy resin, a chain extender, crosslinking agent, plasticizer etc. By controlling the reaction time and the reaction temperature ,we get the polyurethana coatings which composite modified with the sicicone and epoxy resin. By changing theratio ofTDI and PEG, and the addition agent of the silicone, epoxy resin, plasticizer etc, studythe properties of modified polyurethane anti-corrosion paint, and ensure the best ratio nd adding amount. Conclusion shows , when the addition of TDI and PEG ratio is between 1.8:1 to 2.0:1；increase the amount of silicone, epoxy resin, plasticizer are 8%, 7%, 5%；the reaction temperature is 60℃can get the performance of the modified polyurethane paint, the coating had high water absorption strength, good adhesion, low rate, good thermal stability and resistance to acid and base. Key words:polyurethane coating; organic silicon; epoxy resin; modification  主要符号表 TDI 甲苯二异氰酸酯 PEG 聚乙二醇 R 傅里叶转换红外光谱 R值 -NCO与-OH的摩尔比 目录 摘要 I Abstract I 主要符号表 II 1 绪论 1 1.1前言 1 1.2 聚氨酯防腐涂料的改性的研究进展与发展趋势 1 1.2.1 研究进展 1 1.2.2 发展趋势 2 1.3 聚氨酯防腐涂料的防腐机理 3 1.3.1涂膜的屏蔽隔离作用 3 1.3.2 涂膜的缓蚀、钝化作用 3 1.3.3 电化学保护作用 3 1.4 聚氨酯防腐涂料的分类 3 1.4.1单组分潮气固化型聚氨酯防腐蚀涂料 3 1.4.2湿气直接固化聚氨酯涂料 4 1.4.3烘干型封端聚氨酯涂料 4 1.4.4双组分聚氨酯防腐蚀涂料 5 1.4.5 丙烯酸聚氨酯防腐蚀涂料 5 1.4.6 含氟聚氨酯防腐蚀涂料 6 1.4.7 有机硅改性的聚氨酯防腐蚀涂料 6 1.4.8 纳米改性的聚氨酯防腐蚀涂料 6 1.4.9 聚氨酯粉末涂料 7 1.4.10高固体分聚氨酯防腐蚀涂料 7 1.5 实验原料的性能与化学结构 7 1.5.1 甲苯二异氰酸酯（TDI） 7 1.5.2 聚乙二醇（PEG） 8 1.6 本实验的主要内容 8 2 实验部分 1 2.1 实验原理 1 2.2 实验药品 1 2.3 实验仪器 1 2.4 实验步骤 1 2.4.1 实验前水处理 1 2.4.2 预聚体的制备 1 2.4.3 涂料的制备 1 2.4.4 涂膜的制备 1 2.5 分析与测试 1 2.5.1 红外光谱测试 1 2.5.2 差示扫描量热仪（DSC）的表征 2 2.5.3抗酸、碱、盐的测试 2 2.5.4 耐水性、耐溶剂性的测试 2 2.5.5 拉伸强度的测定 2 3 结果与讨论 3 3.1