D022Al3Ti在常压和高压下电子结构的第一性原理研究汇总.doc

D022-Al3Ti在常压和高压下电子结构的第一性原理研究 摘 要：D022-Al3Ti属面心四方结构，滑移系较少，变形较为困难，脆性较大，同时也是含铝量最多的金属间化合物。但是由于室温塑性、韧性太低，利用计算机模拟技术，应Materials Studio 5.5 CASTEP软件，通过使用第一性原理研究方法 关键词：第一性原理能带结构；电子结构；压强；势函数 First-Principles Study Of Electronic Structure For D022-Al3Ti At Ambient And High Pressure Abstract：D022-Al3Ti is a face-centered tetragonal structure,less slip systems, deformation is difficult,brittle,but also the maximum amount of aluminum intermetallic compound. However, due to room temperature ductility, toughness too low,so is still in the basic research stage,has not been implemented widely.In this paper,we use computer simulation technology,Materials Studio 5.5 CASTEP software, By using first-principles methods for modeling,optimization and computing,made D022-Al3Ti under different pressure and different Trial function situations,get the Band structure、Density of states、Charge density and Differential charge density.And comparison of the various figures from their D022-Al3Ti influence various aspects of the electronic structure and analysis.The results show that, pressure on D022-Al3Ti electronic structure of larger,trial function is relatively small. Key words:First-Principles;electronic structure; Pressure；Potential function 目 录 1 绪论 1 1.1 Al3Ti简介及其研究现状 1 1.1.1 D022-Al3Ti的简介 1 1.1.2 D022-Al3Ti的研究现状 1 1.2 本课题的研究内容和目的 2 1.2.1 研究内容和方法 2 1.2.2 研究目的和意义 2 1.3 第一性原理简介 3 1.4 CASTEP软件简介 4 1.4.1 CASTEP软件的主要理论 4 1.4.2 CASTEP软件的基本应用 5 1.5 有关第一性原理密度泛函理论的简介 6 1.5.1 Hohenberg-Kohn定理 6 1.5.2 Kohn-Sham方程 7 1.5.3 结构优化 7 1.5.4 赝势法 8 1.5.5 局域密度近似（LDA）和广义梯度近似（GGA） 9 1.6 本课题的建模及计算思路 9 2 能带结构和态密度 10 2.1 能带结构的概念 10 2.1.1 能带的由来 10 2.1.2 费米面 10 2.1.3 布里渊区 11 2.1.4 D022-Al3Ti的能带结构 11 2.2 态密度 13 3 不同压强下D022-Al3Ti的电子结构 21 3.1 D022-Al3Ti的电荷密度 21 3.2 D022-Al3Ti的电荷密度差分 23 4 结论 25 参考文献 26 致谢 28  1.1 Al3Ti简介及其研究现状 钛铝系金属间化合物主要包括Ti3Al，，(3.3g/cm3)比TiAl还小，Al含量的增加也得到了明显的改善，而且Ti在Al中的扩散速率低，Al3Ti与Al基体的错配度小(2.0%)[1]，，。 ， 1.1.1 D022-Al3Ti的简介 D022型的Al3T晶胞中含2个Ti原子和6个Al原子4个Al1原子