NdFeB永磁材料的成相研究及相关磁性能.docxVIP

PAGE \* MERGEFORMAT18 NdFeB永磁材料的成相研究及相关磁性能 刘宇 （北京科技大学 材料科学与工程学院 北京 100083） 摘 要 通过对Nd-Fe-B永磁材料的Nd-Fe二元系相图，Nd-Fe-B三元系相图（包括室温等温截面，1000℃等温截面，过Nd2Fe14B点的等硼和等Nd垂直剖面相图等）进行分析研究，得出其相关成相规律。同时结合Nd-Fe-B材料各种制备工艺及实际产品特点，进而分析各种成相规律对Nd-Fe-B材料相关磁性能的影响。 关键词 Nd-Fe-B永磁材料；相图；磁性能 Researches of Nd-Fe-B Magnetic Materials’ phase forming and relational magnetic performances Liu yu University of Science Technology Beijing School of Materials Science and Engineering Beijing 100083 ABSTRACT By analyzing and researching he Nd-Fe-B permanent magnet materials Nd-Fe binary phase diagram, Nd-Fe-B ternary phase diagram (including room temperature isothermal section, 1000 ℃ isothermal section, via Nd2Fe14B point equal B and equal Nd vertical cross-section phase diagram etc.), come into related phase forming rules. Meanwhile, Combined with Nd-Fe-B materials of various preparation and actual product characteristics, analyze the impact of various rules on phase Nd-Fe-B magnetic materials performance. KEY WORDS Nd-Fe-B Magnetic Materials; phase diagram; magnetic performance 0 引 言 作为第三代稀土永磁材料，Nd-Fe-B合金具有十分优秀的室温永磁性能，且较之第一、二代永磁材料，Nd-Fe-B合金成本低廉，工艺简便，这种新型高性能的永磁合金不仅引起了磁性材料工作者的兴趣，同时其广阔的应用前景也吸引了大量市场投资者们的注意，对推动科技进步和发展经济有着巨大的作用。同其他材料一样，Nd-Fe-B合金的磁性能与其微观组织密不可分，不同微观组织下的磁性能想去甚远，通过分析Nd-Fe-B合金的显微组织，来制备所需性能的用材料，是磁性材料研究的一个重要手段。本文通过相图分析研究Nd-Fe-B合金的相关成相规律，结合其制备工艺和成分变化过程，得到Nd-Fe-B合金的磁性能与相变过程的关系。 1 相图分析 1.1 Nd-Fe 二元系相图 由于NdFe2的存在与否, 对Nd-Fe-B三元系相图画法的正确性以及在讨论其它相的存在对新型永磁合金性能影响时至关重要，故首先讨论NdFe2存在的可能性。 图1 Nd-Fe二元系相图[1] 各相区成分如下所示： Ⅰ=α-Fe+Nd2Fe Ⅴ=L+γ-Fe Ⅱ=Nd2Fe17+α-Nd Ⅵ=L+δ-Fe Ⅲ=L+Nd2Fe17 Ⅶ=α-Nd+L Ⅳ=Nd2Fe17+γ-Fe Ⅷ=β-Nd+L 如图1所示，在该相图中, 只有一个Nd2Fe17包晶化合物存在,Nd2Fe17属于Th2Ni17结构，六角晶系，a=8.59à，c=12.47à。包晶反应温度为1190 ℃ ,Nd2Fe17与Nd的共晶温度为647℃ , 共晶点成份在Nd含量为75at.%处，物相分析和该体系的磁性测量结果确认NdFe2化合物是不存在的[2]。 从图1中可见, 共晶温度与Nd和Fe的熔点相差甚远,常称这种相图为“深共晶相图” , 具有深共晶的体系容易形成非晶态, 即无序状态容易亚稳到室温。由于这一性质的存在, 所以不经长时间退火的合金,衡射照片很不清楚。退火处理的作用, 一是均匀化, 去应力；二是部分非晶的晶化[3]。我们关心的Nd-Fe-B 三元永磁合金, B含量很低, 其热学性质与N d 一Fe二