钢骨架聚乙烯复合管硫铵生产中的应用.docVIP

PAGE  PAGE 6 钢骨架聚乙烯复合管在硫铵生产中的应用 单 位： 山西焦炭集团益兴焦化 股份有限公司 姓 名： 翟泽军 现任专业 技术职务： 技术员 The application of steel-reinforced plastic composite pipes in ammonium sulfate production 关键词：钢骨架塑料复合管；应用；耐酸性；防漏效果；经济效益 摘 要：介绍了山西省焦炭集团益兴焦化股份有限公司90万吨/年焦炭生产中，利用钢骨架塑料复合材料解决了化产硫铵系统以往出现的母液管线由于腐蚀造成母液外漏，影响生产停车﹑酸耗高的问题，同时有助于硫铵产品质量的提高，稳定煤气质量，产生了较好的经济效益。 Key words:steel-reinforced plastic composite pipe ；application；acid resistance；leakproof effect；economic benefits Abstract：The paper Introduced in Shanxi Province Coke Group Yixing coking Limited by Share Ltd 900000 tons / year Coke production,Use of steel skeleton plastic composite materials solved production of ammonium sulfate system appearing before the mother liquor pipeline by corrosion caused liquid leakage, leaded to the problem that production of parking and high acid consumption, at the same time have a better economic efficiency on help to improve the quality of ammonium sulfate, stability of gas quality. 钢骨架聚乙烯复合管在硫铵生产中的应用 一、前言 山西省焦炭集团益兴焦化股分有公司长期以来极为重视技术进步，依靠先进的管理以及不断提高设备装置的技术水平，从而带动生产的安全运行及产品质量的提高，取得了较好的经济效益。公司90万吨配套化产硫铵系统于2008年2月投产，系统度过了约一年的稳定期后，硫铵母液不锈钢管线焊缝频繁出现漏点，大量母液外泄，影响生产。通过2009年6月全系统管线进行了全面的技术改造，将原有的不锈钢管更换为钢骨架塑料复合管，系统一直能稳定运行，管线至今未出现一处漏点，极大的保障了生产系统的运行。本文通过改造前后系统生产情况的对比，全面分析新材料应用给硫铵生产带来的良好效果。 二、存在问题 硫铵系统自投产开始至随后的近半年内，基本未出现任何管线漏点。但在2008年9月份后，管材的问题逐步凸显出来。硫铵母液管线原为316L不锈钢材料,由于管线材质成份、焊接工艺、焊条材质等方面中出现的缺陷，使得焊缝及管道本体从2008年8月份开始频率出现漏点，且频次成逐月上升趋势。由于漏点多次出现，造成母液大量外泄，不仅使得吨硫铵耗酸大幅攀升，且严重污染环境，同时处理漏点频繁停车，使得煤气含氨超标，影响粗苯生产，硫铵系统生产平衡被大破，产品质量无法保证，总之给整个煤气净化系统的生产带来较大负面影响（附2008年8月至2009年4月硫铵管线漏点及耗子酸等情况统计表）。 2008年至2009年硫铵管线漏点统计表 时间2008年8月2008年9月2008年10月2008年11月2008年12月2009年1月2009年2月2009年3月2009年4月漏点次数1次3次2次5次5次10次9次6次8次停车次数0次0次0次1次2次3次3次2次2次煤气含氨超标次数0次1次1次3次5次6次5次3次5次耗酸（千克/吨硫铵910925940935965980976953990 三、原因分析 理论上硫铵母液管线应采用316L材质，焊接要采用与此材质相符的A022焊条。在管线焊接时要严格按照规程焊接。但由于具体实践过程中的某些环节出现偏差，易导致管材及焊接质量无法保持其耐腐蚀性。 由于硫铵母液属于强酸具有很强的腐蚀性。 3 16L材质的具体