复合助剂改性砂浆力学性能研究.pdf

掺入有助于提高界面剂砂浆的抗折强度，且掺量4％时抗折强度达到最大值。但是，随着乳胶粉 掺量的增加，界面剂砂浆的抗压强度随之降低。 8 胶粉掺量低于4％时，折压比随其掺量的增加提高比较明显，胶粉掺量高于6％以后， 折压比不再增加。乳胶粉的掺入口J以提高界面剂砂浆的折压比，改善砂浆的韧性。 9 掺入胶粉能显著改善界面剂砂浆的粘结性能。随着胶粉掺量的增加，粘结强度呈现上 胶粉掺量8％时，28d粘结强度上升到1．28MPa，是不掺入胶粉的1．46倍。 关键词：罩面修复砂浆：界面剂砂浆；复合助剂；乳胶粉；消泡剂；硅粉；粘结强度；折压 比；收缩：力学性能 II Abstract In causedsalt and coldsaline-alkalineareasofChina,denudation by corrosion，freezingabrasion， isa ofconcrete thereisno in willleadtoconcrete prominentproblem pavement．If repairtime，it structural thataffectstheservice atthedenudation pavement damage，SO life．Therefore，aiming characteristicsofconcrete incoldsaline-alkaline anewconcrete pavement areas，todevelop pavement environment not an forscience materialwhich tothe conditionsis repair adapts onlyurgentrequirement in alsohasan and to theconcrete coldsaline-alkaline technology areas，but important repair pavement fornewconcl．ete construction． guidingsignificance pavementengineering themethodof testand factor differenttest to test,this Using orthogonalsingle paperapplies plans thesurfacemortarandthebase theirmechanical arestudied mortar,particularly properties fume water-binder andsilica are ratio，cement-sandratio，latexpowder-5044N systematically．The ofsurfacemortar．Themechanicalof with mortar,mixed chosen鲢parameters propertiesoverlayrepair the which latex andsilicafumearestudiedwiththemethodof test．Andbasemortar powder orthogonal actsaSinterracialchooseswater-binder agent ratio，cement-sandratio，latexpowder-5010N， and celluloseetheras antifoaming fume，dispersingagent methyl parameters．Using agent,silica testand factortestmethodto themechanical ofinterface orthogonalsingle study properties agent mixedwith fumeandother mortar latex powder-5010N，antifoamingagent,silica polymers．Analyzing themechanicalofthe additivessuchas composite bendingstrength，compressionstrength， properties modulusand bending-compressionratio，bondingstrength,elasticityshrinkingpercentage，main conclusionsaredrawn船follows： is whenthe ratio