天然高分子PBS复合流变学特性探析.doc

天然高分子/PBS复合材料的流变学特性 概述 摘要：通过物理改性提高聚丁二酸丁二醇酯(PBS)的性能重要研究方向本文了近年天然高分子/PBS复合材料，并对天然高分子/PBS复合材料发展作了总结和展望。 关键词：聚丁二酸丁二醇酯；天然高分子；共混改性 中图分类号：TQ31 文献标识码：A Abstract: By adding the natural polymer materials to improve the performance of poly(butylene succinate) (PBS) is an important research direction. The rheological properties of the composites related to the internal structure of the viscoelastic information. The rheological properties can reflect the system of prescription composition directly or indirectly, the relationship between microstructure and processing performance and macro performance, which for practical machining of guide product has very important value.?In this paper, the rheological properties of natural polymer /PBS composites were introduced, and the development of the research on the rheology of natural polymer /PBS composites was summarized and prospected. Key words: Poly(butylene succinate); natural polymers; composites;rheological property 1 前 言 聚丁二酸丁二醇酯（PBS）是由1,4-丁二酸和1,4-丁二醇通过共聚反应合成的半结晶脂肪族聚酯，它具有良好的热塑性、分子柔韧性和生物降解性能等优点，成为最具发展潜力的脂肪族聚酯之一[1-5]。但是PBS分子主链是由非极性的酯键和亚甲基结构单元组成，分子间作用力小，内聚能密度较低，因此存在热学和力学性能缺陷，如耐热温度较低，拉伸和缺口冲击强度较低，同时具有熔点低、成本较高等缺点，限制了其更为广泛的应用。近二十年来国内外学者对PBS进行了化学改性和物理共混改性的研究，以提高力学、热学和熔体强度等性能。 采用具有良好能量耗散的纤维、纳米效应的刚性粒子等对PBS基体进行增强改性，引起了国内外学者的广泛关注。在复合材料中，作为连续相的PBS分子与纤维相互接触、交叉、缠绕，起着传递应力的作用，刚性的纤维起到阻碍分子链段运动的作用，实现了力学和热学性能上的大幅度提升[]。天然高分子材料如淀粉、纤维素等，具有品种繁多、价格低廉、可再生等优点，并能在自然界条件下完全降解。当它们与PBS共混后，天然高分子作为增强相，能提高PBS复合材料的力学强度、热学稳定性和生物降解速率，有效的降低成本。 淀粉 大多数淀粉流变学的研究都是在95℃以下进行的，并且剪切速率与食品加工中常用的搅拌速率相关性不大。在加工中，淀粉悬浮液将承受高温和高剪切速率，这将影响到其流变学特性的改变以至于产品特性也随之改变。很多研究者对淀粉糊化过程在最终产品流变学特性的影响作了大量的研究[9]。流变测试分析中采用Herschel-Bulkley方程(如下所示)对流变曲线进行模型拟合分析。 τ=τo+Kγn 式中：τ为剪切应力/Pa；τo为屈服应力/Pa；K为稠度系数/Pa·sn；γ为剪切速率/s-1；n为流动特征指数，无量纲，表示液体偏离牛顿流体的程度。 郭泽镔等[10]讨莲子淀粉糊及莲子淀粉一胶体体系的流变特性，使用流变仪研究了不同莲子淀粉乳浓度和添加不同亲水性胶体的莲子淀粉糊的流变特性。静态流变特性研究结果表明，莲子淀粉糊和添加胶体的莲子淀粉糊均为典型的非牛顿、时间依赖剪切变稀和触变性的流体，其流变特性曲线可用Herschel—Bulkley方程进行较好的拟合。随淀粉乳浓度和瓜尔豆胶(guar)、黄原胶(xan)添加量的增大，莲子淀粉糊的屈服应力τo增大，而添加羧甲基纤维素(CMC)、卡拉胶(car)和海藻酸钠(alg)可