78金属件涂装前纳米转化膜处理技术.doc

金属件涂装前纳米转化膜处理技术 朱丹青 Wim van Ooij1，钟金环,* 王一建 陆国建 (1.美国依科技术公司,美国俄亥俄州,45014; 2.杭州五源公司表面工程研究所,浙江杭州,310030) 摘要：根据涂装金属的腐蚀行为分析，涂层的防腐蚀性能，主要取决于涂层与基体表面的附着力。本文结合传统的磷化处理技术特征，提出了节能环保型的涂装前纳米转化膜处理技术，分别阐述了纳米陶瓷锆盐、硅烷处理金属时在其表面形成的纳米转化膜的处理技术，研究试验结果表明，纳米转化膜均可显著提高涂层与金属基体的附着力，其相应的耐腐蚀性能亦接近或达到了磷化处理方式，已经可满足工业涂装生产中的产品质量技术要求。金属件涂装前纳米转化膜处理技术可广泛地应用于家电、汽车、五金等领域的油漆、粉末及电泳等涂装前处理生产中。 关键词：涂装前处理，附着力，耐蚀性，硅烷处理，锆盐处理 Abstract: According to metal corrosion behavior theory, it is known that the anti-corrosion performance of coatings on metal is mainly depended on its adhesion to metal substrate. In this paper it presents new energy-efficiency and environmental-friendly nanoscale conversion coating technologies. Silane process and nanoceramic process (Zr-based pretreatment) are introduced, respectively. With the nanoscale conversion coating, the performance of adhesion and corrosion resistance of painting films is greatly enhanced, which is close to traditional phosphating process. The quality of product has reached national or industrial standards. By practical application cases in domestic appliance and automobile accessory, etc., the nanoscale conversion coating technologies can be extensively applied in metal coating pretreatment. Keywords: coating pretreatment, adhesion, corrosion-resistance, silane process, Zr-based pretreatment 0.前言 在涂装金属件，增强涂层与基体附着力，磷化处理技术已经有100多年历史。它是一种机械键力的方法[1]，磷化膜使涂层与金属基体形成表面粗糙度(roughness)或基体锚状(anchor pattern)结构有关的嵌锁作用的机械力。图1为锌系磷化膜与钢铁基体的示意图。 磷化后钢铁表面粗糙度增加，比表面积增大，涂层与磷化膜象锚状结构结合，可以十分显著地提高了涂层与基体的附着力。为了提高磷化膜的耐蚀性能，通常还采用了六价铬钝化封闭处理。 由于磷化处理过程中存在表调的碱金属磷化钛盐废液，磷化废液含有磷酸、硝酸等毒害的重金属离子(如Ni2+、Mn2+、Ca2+、Cu2+等)、亚硝酸盐促进剂及磷化残渣，钝化废液含有致癌物质的六价铬，造成严重的环境污染。 随着工业化生产要求，节能减排的环保要求，对涂装前处理工艺、提高热效率，逐步实现零排放，是涂装前处理技术发展的方向和趋势[2]。 1.概述 1.1 涂装金属附着力特性 有机涂层对金属基体的附着力可以分为三种基本类型： 化学键力(chemical bond) 分子间力(intemdecular force) 机械键力(mechamical bond一种机械嵌锁作用力) 通常至少有上述二种这样键力的作用，使涂层与金属件牢固地粘合在一起。 从而可见各种附着键力的本性取决于涂层和基体的界面的过渡层。而基体提供了机械附着力和化学吸引点或极性吸引点，涂层提供将其吸引到金属表面的化学条件。金属加工后工件涂装前放置在大气中，大多数都会形成一种氧化膜，许多情况下工厂经除