ZnS纳米空球论文.doc

ZnS纳米空球/Au/半胱氨酸修饰电极的制备及其在重金属 离子检测中的应用 摘要：本文主要以化学合成法制备出ZnS纳米空球，在制得实验所需的空球之后，再用L-实验的结果显示对重金属离子的检测效果有明显不同，控制因素有，值，不同的缓冲溶液，静止时间。在综合因素的检测和实验结果的表征下，重金属离子的检测峰值最大，效果最佳的是当的值为5，乙酸缓冲溶液，静置60S左右，用-0.2—0.4的扫描电压扫描。 关键词：ZnS，纳米空球，重金属离子，检测 Preparation of electrode modified by ZnS nanoseres/ Au /cysteine and application of heavy metal ions in the detection Abstract:Article mainly in chemical synthesis of the ZnS nano hollow ball, administered in needed for the experiment was empty after the ball, with L - cysteine modified electrodes, and finally to detect heavy metal ions. Experimental results show that the detection effect of heavy metal ions are obviously different, control factors, the pH, different buffer solution, the rest time. The comprehensive factors of detection and characterization of the experimental results, the heavy metal ions detection peak is the largest, best is when the pH value is 5, acetic acid buffer solution and let stand for about 60 s, with a pH of 0.2-0.4 scanning voltage scanning. Key words: ZnS; hollow nanospHeres; heavy metal ion 1. 前言： ZnS是一种重要的Ⅱ-Ⅵ族半导体材料,当ZnS颗粒的半径小于或接近于激子波尔半径的时候，由于量子尺寸效应、奇特的线性和非线性光学效应，导致物理性能较宏观物体发生很大的变化。在光、电、磁、催化等方面具有巨大的应用潜能[1]（如发光二极管、光催化[2]、传感器、红外窗口材料、电致发光等领域），因而成为人们的研究热点之一。最新的当属刘红梅[3]等采用电化学方法装配出单层的ZnS纳米微粒的研究，该实验研究了ZnS的结构性能和光电应用和最新的科学成果。 制备ZnS纳米微粒的方法有多种，如微乳液法[4]、溶剂热法[5]均匀沉淀法[6]、电沉积法[7]、聚合物网络合成法[8]等。目前重金属污染已成为一种严重的环境污染，研究对重金属离子的检测具有十分重要的实际意义，因而受到大量科学工作者的重视。唐国林[9]等基于QCM（Quartz Crystal Microbalance,石英微天平分析）技术，采用纳米金信号增强压电示金属检测方法对铜、汞、铅、镉等进行了检测，结果表明该法检测灵敏度高且易于实现。付海曦[10]等对水中的重金属离子检测做出了试验方法，让我们能够从一定程度上解决重金属离子水质污染。结果表明:经简单的电化学清洗步骤即可高重现地再生电极表面,大幅度提高检测Pb2+、Zn2+的灵敏度,检测范围也可拓展至高卤素离子含量的样品。虽然近年来ZnS越来越多地用于电化学方面的研究，但在重金属离子检测中的应用却很少。本文以溶剂热法制得ZnS纳米空球，并分别用其和氯金酸、L-半胱氨酸修饰制备电极，以乙酸-乙酸钠缓冲溶液为检测溶液[11]，研究了电极对重金属离子检测及影响因素。 2 实验部分 2.1 实验试剂： 试剂：ZnSO4：AR，中国医药（集团）上海化学试剂公司； 乙二胺：AR，天津市化学试剂厂; 无水乙醇：AR，天津市化学试剂一厂； CS2：AR，成都科龙化工试剂厂； 醋酸-醋酸钠缓冲溶液(=4、5、6); 磷酸缓冲溶液(=5)氯金酸; KCL溶液(0.1M KCl+0.01M HCl，=5); L-半胱氨酸：AR，郑州诚旺化工有限责任公司 ； 铁氰化钾溶液（0.05M K3Fe(CN)6+0.1M KCl）。 2.2 实