在不同电压下表面电聚苯胺对稀土-镁-镍基贮氢合金电化学性能的影响.docVIP

在不同电压下电镀聚苯胺对La-Mg-Ni基贮氢合金 电化学性能的影响 本文研究了在电镀电压为1 V、2 V、3 V电镀时间为1.5 min条件下电镀聚苯胺对基贮氢合金电化学性能的影响。电化学测试表明：经表面镀覆聚苯胺后，基的高倍率放电性能均有所提高合周S200从78.89 %分别提高到82. %、83.19 %、81.89 % （1 V、2 V、3 V）基ffect of surface modification of La-Mg-Ni-based hydrogen storage alloy with polyaniline by electroless deposition at different voltages on electrochemical properties Abstract: A new polyaniline PANI -coated technique by electroless deposition at different voltages 1 V，2 V，3 V and at 1.5 min was adopted for a La-Mg-Ni-based hydrogen storage alloy. Electrochemical tests indicate that the maximum discharge capacity, t