碳钢管酸洗和钝化工艺.docVIP

碳钢管酸洗和钝化工艺Pickling and passivation technics for Carbon steel pipe工艺材料：工艺流程：产品名称Name of product产品代号Code name of product主要成分Bases 功能用途Capacity and application除锈剂Rust removerCA-66盐酸、缓蚀剂Hydrochloric，Corrosion inhibitor除锈、除氧化皮Rust cleaning,Oxide skin cleaning.除锈助剂Pickling additives BR-101A表面活性剂等Surface active agent ,etc.脱脂，增强酸洗能力。Strengthen the acid pickling capacity.酸雾抑制剂Acid fog inhibitorBN-111JFC,十二烷基硫酸钠JFC,sodium dodecyl sulfate，etc抑制酸雾挥发Control the acid fog volatilize .白钢酸洗剂Stainless steel pickling agent BL-612硝酸、植酸等Nitric acid ,Phytic acid，etc白钢表面酸洗及钝化Pickling and passivation of the stainless steel 皮膜钝化剂PassovatorTS-300三乙醇胺，碳酸钠等Trolamine ,soda.etc封闭金属表面，形成保护膜。Seal off the metal surface ,from a resist film.除锈除油二合一处理→中和处理→皮膜钝化处理→自然干燥→管件外部涂防锈剂。Process:Rust removing and oil cleaning at one time →Neutralization→passivation→Natural drying →Coat the pipe outside with Antirust .防锈除油二合一处理槽：Rust removing and oil cleaning tank:按体积比：BR-101A ：CA-66：水＝１：６：３配制工作液。当大气气压低或者天气有雾时，按１％向槽内加入ＢＮ－１１１酸雾抑制剂，用来控制槽液酸雾挥发。As the ratio by volume to make the working solution .When the HYPERLINK app:ds:atmos \t _self atmos is low or there is any fog , add 1% Acid fog inhibitor BN-111 by volume .中和处理槽：Neutralizer Tank :春、夏、秋季时：按重量比8~10%加入中和剂BH-008配制工作液。冬季气温低时：按比重3~5%加入TS-300配制工作液。春夏秋工件以中和为主；冬季以清洗为主。In the season of spring ,summer and autumn :Add Neutralizer BH-008 8~10% by weight to make the working solution .In winter ,when the temperature is low :Add Passivator TS-300 3~5% by weight to make the working solution .皮膜钝化处理槽：Passivation tank :按重量比10~15%加入水质调节剂TS-300配制工作溶液。Add Passivator 10~15% by weight to make the working solution .工作槽液的工艺参数：technic data for the Working solution liquid in the tanks :除锈除油二合一处理槽：常温浸渍，时间：30~90min，PH值≤1.5Rust removing and oil cleaning tank: soakage at the normal temperature , time :30~90min ,PH≤1.5 .中和槽：春夏秋季：PH≧12，常温浸渍时间3~5min；冬季PH≧9，浸渍时间3~5min，温度30℃左右。Neutralizer Tank :In the season of spring ,summer and autumn : liquid PH PH≧12, soakage time 3~5min; In winter PH≧12,