防腐抗渗溷凝土工艺原理及工程实践 防腐抗渗混凝土工艺原理及工程实践 千鹤茂　单　咏 (鞍山市双鼎商品混凝土有限责任公司　鞍山　 114045) 摘　要 :某 3 200m3大型现代化高炉冲渣 ( INBA)泵房冷却塔混凝土集水槽 ,C30 P8且有耐碱要求。在分 析混凝土渗漏原因和防腐机理基础上 ,提出了配制这种混凝土的技术要点 ,并取得相应效果。但在施工实践 中由于忽略养护和防水构造不规范等原因而呈现局部浸渗水缺陷。根据混凝土的细微观结构及其膨胀、致 密、毛细通道填充等工艺原理进行妥善处理 ,取得较好效果。 关键词 :湿胀干缩　渗水通道　微裂纹　有害孔 IMPERMEABILITY CONCRETE AND ITS PROJECT PRACTICE Qian Hemao　Shan Yong THE TECHNICAL PRINCIPLES OF ANTICORROSIVE AND should have alkali -resistance when using it for cooling tower’s catch basin of a flushing pump house of a large modern blast furnace (3200m3) 1 It was presented the technical points of peparing this concrete based on analyzing its anticorrosive mechanism1 It was also described through a project the method of treating local water seepage of this sort of concrete1 Keywords :wet expansion and dry shrinkage　water seepage pass　microcrack　harmful pore (Anshan Shuangding Commercial Concrete Co1 ,Ltd　Anshan　114045) Abstract :The concrete C30 P8 　　刚性防水结构的效果如何 ?曾一度成为工程技冷却塔集水槽槽体混凝土 ,必须是耐碱混凝土。 术界争议的热点问题 ,通过具有防腐、抗渗要求的工东 INBA冷却塔集水槽共 4个 ,呈上大下小倒 程结构施工实践 ,证明选材得当 ,措施到位 ,是可以四角棱台形状 ,其尺寸为 850 mm ×850/ 1200 mm × 达到预期效果的。 1200 mm ×4000 mm (A ×A/ B ×B ×H) ,槽壁厚 300 m m,采用 C30 P8耐碱防水混凝土。 1　工程概况 某容积为 3 200 m3高炉 ,是一座改进串罐或无2　耐碱抗渗混凝土配制工艺原理 料钟炉顶 ,内然式热风炉的现代化高炉。熔渣经沟21 1　耐碱骨料及掺合细粉选择 槽进入水渣槽 ,在冲制箱高速水流作用下粒化成水粗骨料选用石灰石 (CaCO3 ) ,50 mm ×50 mm 渣。冲渣水从转鼓分离出来后进入下部的集水槽×50 mm立方试样抗压强度平均 871 6 MPa ,压碎 中 ,溢流进热水池 ,再进热水泵打入冷却塔。冷却水性指标 71 8%,属碱性骨料 ,Ⅱ级级配区 ,控制含泥 进入下部集水槽中 ,再经粒化泵送至冲制箱中循环量 01 5%,细骨料为河砂 ,选用水渣微粉 ,其细度比 使用。碱性渣的冲制水呈 P H12 -14弱碱性 ,因而 ,表面积 S=5 420 cm2/g,化学成份如表 1所示。 表 1　水渣微粉化学成分 化学成分 / % 碱度 R 活性率 MC 质量系数 K 材料名称 CaO SiO2 Al2 O3 MgO Fe2 O3 SCaO + MgO SiO2 + Al2 O3Al2 O3 SiO2CaO + MgO + Al2 O3 SiO2 + Mn2 O5 + TiO2 水渣微粉掺合料 371 5 331 82 141 53 121 01 1186 0116 11 02 01 43 315 　　由表 1可看出 :水渣微粉碱度 R大于 1,活性率 Mc 01 20 ,达 01 43是较好的掺合细粉。 作　　者 :千鹤茂　男　 1956年 6月出生　高级工程师 21 2　最小空隙率、最小水灰比原理 收稿日期 :2008-05-10 　　　 Industrial Construction Vol138 , Supplement ,2008