HDPESpecification.docVIP

№ Properties 153-02 K 153-10 K Top grade First grade Top grade First grade 1 Density, g/cm3 0.9185-0.922 0.9185-0.922 - 2 Melt flow rate, g/10 min 0.21-0.39 0.21-0.39 0.21-0.39 0.21-0.39 3 Spread of Melt flow rate within the party, %, max +/- 8 +/- 12 +/- 8 +/- 12 4 Amount of inclusions, max units 3 15 - 5 Mass fraction of volatile substances, %, max - 0.07 0.1 6 Mass traction of ash, %, max - - 7 Resistance to cracking, hrs, min 500 500 8 Tensile Strength at Yield, MPa, kg/cm2 , min 9.8 100 9.8 100 9 Tensile Strength at Break, MPa, kg/cm2 , min 13.7 140 13.7 140 10 Elongation at break, %, min 600 600 11 Mass fraction of extractables, %, max 0.5 0.6 0.5 0.6 № Properties 271-274 K Top grade 1 Density, g/cm3 0.950-0.955 2 Melt flow rate, g/10 min 0.3-0.65 3 Spread of Melt flow rate within the party, %, max +/- 8 4 Amount of inclusions, max units 3 5 Mass fraction of volatile substances, %, max 0,1 6 Mass fraction of ash, %, max 0,05 7 Resistance to cracking, hrs, min 500 8 Tensile Strength at Yield, MPa, kg/cm2 , min 22.6 230 9 Tensile Strength at Break, MPa, kg/cm2 , min 21.6 220 10 Flexural Modulus, kg/cm2 588-833 11 Elongation at break, %, min 600 12 Oven aging, hrs, min 8